CeO x -Decorated NiFe-Layered Double Hydroxide for Efficient Alkaline Hydrogen Evolution by Oxygen Vacancy Engineering.

Xixi Wang,Yu Yang,Lechen Diao,Yu Tang,Fang He,Enzuo Liu,Chunnian He,Chunsheng Shi,Jiajun Li,Junwei Sha,Shuaihua Ji,Ping Zhang,Liying Ma,Naiqin Zhao

DOI: https://doi.org/10.1021/acsami.8b11688

IF: 9.5

2018-01-01

ACS Applied Materials & Interfaces

Abstract:As a promising bifunctional electrocatalyst for water splitting, NiFe-layered double hydroxide (NiFe LDH) demonstrates an excellent activity toward OER in alkaline solution. However, its HER activity is challenged owing to the poor electronic conductivity and insufficient electrochemical active sites. Therefore, a 3D self-supporting metal hydroxide/oxide electrode with abundant oxygen vacancies is prepared by electrodepositing CeOx nanoparticles on NiFe LDH nanosheets. According to the DFT calculations and experimental studies, the oxygen vacancies at the NiFe LDH/CeOx interface can be introduced successfully due to the positive charge accumulation resulting from the local electron potential difference between NiFe LDH and CeOx. The oxygen vacancies accelerate the electrons/ions migration rates, facilitate the charge transfer and increase the electrochemical active sites, which giving rise to an efficient activity toward HER in alkaline solution. Futhermore, NF@NiFe LDH/CeOx needs a lower potential of 1.51 V to drive a current density of 10 mA cm-2 in overall water splitting and demonstrates a superior performance compared with the benchmark Pt/C and RuO2, which indicating to be a promising candidate bifunctional electrode catalyst.