The Effect of Cubic-Texture on Fatigue Cracking in a Metastable Β Titanium Alloy Subjected to High-Cycle Fatigue

Zhihong Wu,Hongchao Kou,Nana Chen,Zhixin Zhang,Fengming Qiang,Jiangkun Fan,Bin Tang,Jinshan Li

DOI: https://doi.org/10.1016/j.ijfatigue.2020.105872

IF: 5.489

2020-01-01

International Journal of Fatigue

Abstract:In this work, stress-controlled high-cycle fatigue tests were performed on Ti-7Mo-3Nb-3Cr-3Al alloy with beta-cubic texture to investigate fatigue crack-initiation mechanisms and microstructurally small fatigue crack growth behaviors. The S-N curve shows a general feature of monotonic increase in the mean lifetime with decreasing stress level. Fatigue crack-initiation sites revealed the contiguous beta facets. The fracture surface observations and the slip trace analysis show that most faceting occurred in {110} < 111 > slip system with the highest Schmid factor. Besides, a higher Kernel average misorientation (KAM) was found in fatigued microstructure. This strain localization would contribute to the fatigue crack-initiation process.