Abstract:High temperature is an important factor affecting the mechanical properties and crack propagation behavior of granite. In this study, the mechanical properties and thermal damage mechanism of granite after high temperature are studied experimentally. Subsequently, based on the content and distribution of granite minerals, combined with computed tomography (CT) technique and grain-based model (GBM) modeling method, a novel discrete element numerical model considering real mineral distribution is introduced, and the rationality of the method is verified by experiments. On this basis, the mechanical behavior, crack propagation behavior and failure mode of granite after high temperature are studied. The results show that 450 °C is the thermal damage threshold of granite in this study. When T ≤ 450 °C, the development of thermally-induced microcracks is not significant, the P-wave velocity of granite decreases slightly, and the change of mechanical properties is not obvious. When T > 450 °C, the thermally-induced microcrack propagates rapidly, the fracture network and fracture zone are formed locally in the specimen, and the P-wave velocity and mechanical properties of granite deteriorate significantly. The simulation results show that the number of thermally-induced microcracks in granite specimens is positively correlated with temperature, and the tensile cracks are mainly at the mineral boundary, and the thermal stress concentration between mineral particles is the main cause of thermally-induced microcracks. After temperature treatment, there are mainly tensile cracks in granite specimens under uniaxial compression, and the orientation of tensile cracks tends to be isotropic with the increase of temperature. When T < 600 °C, the crack distribution and failure mode of granite specimens under uniaxial compression are consistent with those at room temperature. When T ≥ 600 °C, thermally-induced microcracks begin to dominate the uniaxial compression failure process, and granite specimens begin to show ductile failure characteristics, and the brittle-plastic transition was observed between 600 °C and 750 °C.

Fracture Mechanics Behavior of Jointed Granite Exposed to High Temperatures

Experimental investigation on damage characteristics and fracture behaviors of granite after high temperature exposure under different strain rates

Tensile Microcracking Behavior of Granites after High Temperature Treatment by Considering the Effect of Grain Size and Mineralogical Composition

Experiment Study on Shear Behavior and Properties of Granite Fractures under Real-time High-temperature Conditions

Mechanical Behaviour and Failure Modes of High-Temperature Jointed Granite Based on DIC and AE Technology

Experiment and numerical simulation study of dynamic mechanical behavior of granite specimen after high temperature treatment

Real-time Experiment Investigations on the Coupled Thermomechanical and Cracking Behaviors in Granite Containing Three Pre-Existing Fissures

Tensile Properties and Damage Evolution Laws of Granite After High- and Low-Temperature Cycles

Investigation of the fracture characteristics of granite and green sandstone under different thermal treatments

Mechanical Properties and Crack Propagation Behavior of Granite After High Temperature Treatment Based on a Thermo-Mechanical Grain-Based Model

Experimental Study on Damage and Fracture Characteristics of Beishan Granite Subjected to High-temperature Treatment with DIC and AE Techniques

Mechanical properties of granite at high temperature subjected to true triaxial compression

The Sequence of Heating and Loading Affects Shear Properties of Granite Fractures Under High Temperature

Experimental study on mechanical properties and evolution of fracture failure of granite considering initial temperature damage and prefabricated fissure length

Variation of mechanical properties of granite after high-temperature treatment

Mechanical behavior of granite subjected to thermal treatment: insight from experiment and numerical simulation

Effects of high temperature and thermal cycles on fracture surface's roughness of granite: An insight on 3D morphology

Effects of Pre-Existing Cracks and Temperature on Failure Mode of Granite from Eastern China

Experimental investigation on the mechanical properties of thermally damaged granite specimens containing pre‐existing holes

Structural Properties and Failure Characteristics of Granite after Thermal Treatment and Water Cooling

Experimental and numerical simulation study on the evolution of mechanical properties of granite after thermal treatment