Abstract:The diagram of mineral phase transformation for valuable metal recovery and mesoporous silica in situ preparation from fly ash.
What problem does this paper attempt to address?
The paper aims to address the effective utilization of high-value resources in high-alumina fly ash. Specifically, the research objectives include:
1. **Efficient recovery of valuable metals from high-alumina fly ash**: Such as aluminum (Al), lithium (Li), and gallium (Ga), which are present in high concentrations in fly ash and have significant economic value.
2. **In-situ preparation of mesoporous silica materials**: By selective acid leaching, preparing mesoporous silica materials with high specific surface area and rich pore structure from fly ash.
### Background Issues
- **Large accumulation of fly ash**: The annual production of fly ash continues to increase, accumulating to about 1.4 billion tons, which not only occupies land but also impacts the environment.
- **Limitations of current utilization methods**: Currently, fly ash is mainly used for low-value applications such as building materials and agriculture, failing to fully utilize its high-value resources.
- **Characteristics of high-alumina fly ash**: There are large amounts of high-alumina coal in northern Shanxi and western Inner Mongolia. During combustion, these elements further concentrate in the fly ash, with alumina and silica content exceeding 80%, aluminum mass fraction reaching 35-50%, lithium grade reaching 200-400 ppm, and gallium grade reaching 50-100 ppm.
- **Challenges of stable mineral phases**: Fly ash contains stable mullite and quartz mineral phases, making the efficient extraction of aluminum, silicon, and other resources difficult.
### Research Methods
- **Mineral phase transformation**: By co-activating with sodium carbonate and potassium carbonate, transforming the stable mineral phases in fly ash into soluble mineral phases such as nepheline and albite.
- **Selective acid leaching**: Using hydrochloric acid solutions of different concentrations for acid leaching, studying the dissolution behavior of metals and the mechanism of pore structure formation.
- **Characterization analysis**: Using X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), and other methods to characterize the phase composition, crystal structure, chemical composition, and pore structure of the samples.
### Main Findings
- **Metal recovery efficiency**: Under different acid leaching conditions, the recovery rates of aluminum, lithium, and gallium reached 86.17%, 89%, and 80% (in the K system), and 92.38%, 95%, and 83% (in the Na system), respectively.
- **Preparation of mesoporous silica**: Successfully prepared mesoporous silica materials with high specific surface area (up to 746.76 m²/g) and rich pore structure through acid leaching.
- **Pore structure regulation**: With the increase in acid concentration, the change sequence of pore shape was the same, eventually forming type IV adsorption-desorption isotherms and H3 hysteresis loops, indicating that the materials have good mesoporous structures.
### Significance
- **Technical support**: This research provides technical support for the comprehensive recovery of high-value resources, contributing to the efficient utilization of fly ash.
- **Industrial application potential**: Through efficient separation and comprehensive utilization under mild conditions, it is expected to promote the application of fly ash in fields such as catalysis, adsorption, thermal energy storage, and biomedicine.