A clean and efficient utilization of fly ash with a focus on the strengthening decomposition mechanism of mullite

Jun Hao,Zhi-he Dou,Ting-an Zhang,Kun Wang,Xing-yuan Wan,Song Qi

DOI: https://doi.org/10.1016/j.fuel.2022.126473

IF: 7.4

2022-11-04

Fuel

Abstract:A novel method of comprehensive disposal of low temperature and high-efficiency reduction of fly ash to produce ferrosilicon without slag under the action of Fe 2 O 3 was proposed in this paper. In addition, the promotion of Fe 2 O 3 on the reduction and decomposition of fly ash at a low temperature and the strengthening mechanism of the reduction and decomposition of the mullite phase were systematically studied. The thermodynamic analysis shows that the decomposition reaction of mullite can be carried out only after the free SiO 2 in fly ash is exhausted. Combined with the thermodynamic prediction of the equilibrium phase concentration of reduction products, the phase evolution of reduction products and the results of SEM microanalysis, it is proposed that the carbothermal reduction process of fly ash and the decomposition mechanism of mullite are as follows: iron oxide reduction, mullite decomposition into aluminum–silicon oxide and aluminum–silicon oxide deep decomposition and complete release of Al 2 O 3 , while the final products of reduction decomposition are ferrosilicon phase and alumina. According to the mineralogical characteristics of reduction decomposition products, a novel idea of preparing ferrosilicon and alumina/calcium aluminate byproducts by electric furnace melting is proposed, which lays a theoretical foundation for the large-scale, slag-free and high-value utilization of fly ash.

energy & fuels,engineering, chemical