Abstract:The threat of cascading damage to downstream components caused by the light modulation intensification of laser repaired morphology on the surface of fused silica optics cannot be ignored in high-power laser systems. This paper uses the angular spectrum diffraction theory based on the analysis of repaired surface morphology of CO 2 laser rapid ablation mitigation to study the influence of different repaired morphologies on the downstream 355 nm laser transmission. Studies show that the arc-shaped laser processing lines on the repaired surface are formed by the residual height superposition of the material after laser scanning of two adjacent layers, and the short-pulse laser can substantially suppress the heat-affected zone of the repaired area. The offaxis ring caustic and on-axis hotspot are sequentially generated in the downstream modulated light fields of the conical repaired sites with different diameters. A secondary peak with modulation larger than 3 emerges downstream of the modulation curve.Meanwhile, the maximum modulation and the secondary peak increase with the diameter and cone angle of the repaired site, and the position of the secondary peak appears farther away from the rear surface. The modulations of three repaired sites with cone angles of 15°, 20°, and 25° can finally be stabilized below 3. Overall, the downstream optics should be installed far away from the positions where the maximum modulation and the secondary peak emerge. Additionally, the maximum value and the secondary peak of the downstream light modulation of double repaired sites are larger than that of the single repaired site, and both rise as the repaired sizes increase. Thus, large-scale and large-size repairing of multiple surface damages in the same area should be avoided in the laser repairing of fused silica.

Repaired Morphology Induced Optical Modulation in Fused Silica Based on Scalar Diffraction Theory

Optical Modulation Study of Repaired Damage Morphologies of Fused Silica by Scalar Diffraction Theory

Repaired Morphology of CO 2 Laser Rapid Ablation Mitigation of Fused Silica and Its Influence on Downstream Light Modulation

Material migration and damage characteristics of fused silica optical surface treated by CO 2 laser/short – pulse ultraviolet laser

Optical Modulation of Repaired Damage Site on Fused Silica Produced by CO2 Laser Rapid Ablation Mitigation

Incident Laser Modulation of a Repaired Damage Site with a Rim in Fused Silica Rear Subsurface

Morphology evolution mechanisms and localized structural modification of repaired sites on fused silica optics processed by CO2 laser rapid ablation mitigation

Rapid and Non-Destructive Repair of Fused Silica with Cluster Damage by Magnetorheological Removing Method

Research on Laser-Induced Damage Post-Restoration Morphology of Fused Silica and Optimization of Patterned CO2 Laser Repair Strategy

Numerical simulation of the modulation to incident laser by the repaired damage site in a fused silica subsurface

Research Development of CO2 Laser Treatment for Repair Damage in Fused Silica

Combined Studies of Surface Evolution and Crack Healing for the Suppression of Negative Factors During CO2 Laser Repairing of Fused Silica

Experimental and Theoretical Investigation of Localized CO2 Laser Interaction with Fused Silica During the Process of Surface Damage Mitigation

Formation Mechanism of Bubbles in the Crack Healing Process of Fused Silica Using a CO2 Laser

Repair of Fused Silica Damage Using Selective Femtosecond Laser-Induced Etching

Investigation on the influence of the CO2 laser parameters on the defect healing process of fused silica

A Novel Method to Additively Repair Micro-Damaged Fused Silica Using Localized CO2 Laser

Effects of CO2 Laser Irradiation on Surface Morphology and Stress Distribution of Fused Silica

Evolution of Intrinsic Defects and Ring Structures on the Surface of Fused Silica Optics after CO2 Laser Conditioning.

Correlation Between Photoluminescence Properties of Surface Defects and Laser-Induced Damage Threshold of Fused Silica

Formation Mechanism of Surface Morphology in the Process of CO2 Pulsed Laser Processing of Fused Silica Optics