High-temperature corrosion kinetics of biomass-fired boiler superheater materials

Bo Liu,Xiaoping Chen,Cai Liang,Daoyin Liu,Jiliang Ma

DOI: https://doi.org/10.3969/j.issn.1001-0505.2018.01.012

2018-01-01

Abstract:Aiming at the problems that biomass-fired boiler often experiences chlorine-induced high-temperature corrosion of superheater due to high amount of chlorine in biomass, high-temperature corrosion experiments are conducted on seven types of commercial superheater alloys, i.e. 15CrMoG,12Cr1MoVG,12Cr2MoWVTiB,20G,T91,TP347H and 0Cr25Ni20 using a weight-in-crease method in a horizontal-tube furnace, with temperature conditions and HCl-containing atmos-phere simulating the working conditions of superheater in a biomass-fired boiler.Mass gain curves of the specimens are plotted and corrosion kinetics are studied using thermal analysis kinetics method. The experimental results show that the mass gains fit with parabolic curves and corrosion rates are strongly influenced by temperatures and HCl concentrations.Among the tested alloys,T91,TP347H and 0Cr25Ni20 have better performances against the high-temperature corrosion than the other al-loys,which are attributed to their higher Ni content.The kinetics analysis shows that the high-tem-perature corrosion follows the one-dimensional diffusion model.