Effect of alloy elements on microstructure and properties of EH36 steel joint by FAB submerged arc welding

Lei LIU

DOI: https://doi.org/10.3969/j.issn.1673－4807.2017.06.010

2017-01-01

Abstract:FAB submerged arc welding experiments were conducted on the steel EH36 using different alloy pow-ders,respectively.The comparative research of microstructure and property on the joints were also studied.The results showed that the welding thermal cycles did not lead to softening in heat affected zone(HAZ)of the EH36 steel joint when the weld heat input of FAB were 82.8~97.7 KJ/cm,and the results of strength test of the weld-ing joints also met the requirement of the shipbuilding plate welding standard test.But the low-temperature im-pact toughness of EH36 steel joint decreased heavily when the weld heat input of FAB was 97.7KJ/cm.Howev-er,the toughness of EH36 steel joint by FAB submerged arc welding with high welding heat input 97.2KJ/cm could also be improved when the domestic alloy powder Fe-9 by the proper addition of Mn and Ti elements were used.In the alloy powder Fe-9,the presence of Mn as an alloying element which stabilized the austenite de-creased austenite-to-ferrite transformation temperature, and Ti provided active nucleation sites for acicular fer-rite.The combined action of Mn and Ti in weld metal and fusion zone prohibited the growing of proeutectoid fer-rite and promoted the formation of acicular ferrite.