Abstract:E36 ship plate steel was, respectively, produced by as rolling and normalizing process (ARNP), and EH36 and FH36 ship plate steel was produced by the thermo-mechanical control process (TMCP) with low carbon and multi-element micro-alloying. The microstructure of the three grades of ship plate steel was composed of ferrite, pearlite, and carbides at room temperature. The average grain size on 1/4 width sections (i.e., longitudinal sections) of the three grades of ship plate steel was, respectively, 5.4 μm, 10.8 μm, and 11.9 μm. EH36 and FH36 ship plate steel had the higher strength due to precipitation and grain boundary strengthening effect, while the E36 ship plate steel had the lower strength due to the recovery phenomenon in the normalizing process. EH36 and FH36 ship plate steel had higher impact toughness due to lower carbon (C) and silicon (Si) content and higher manganese (Mn) content than E36 ship plate steel. E36 ship plate steel had the best plasticity due to the two strong {110} and {111} texture components. The fracture toughness KJ0.2BL(30) values of E36 and EH36 and KJ0.2BL value of FH36 ship plate steel were, respectively, obtained at 387 MPa·m1/2, 464 MPa·m1/2 and 443 MPa·m1/2. EH36 and FH36 ship plate steel had higher KJ0.2BL(30) due to lower C and Si and higher Mn, niobium (Nb), vanadium (V), and aluminum (Al) content than the E36 ship plate steel. The fatigue crack growth rate of E36 ship plate steel was higher than that of EH36 and FH36 ship plate steel due to its higher carbon content and obviously smaller grain size. The analysis results and data may provide a necessary experimental basis for quantitatively establishing the relationship between fracture toughness, yield strength and impact toughness, as well as the relationship between fatigue crack growth rate and both strength and fracture toughness.

Comparison of Microstructure and Mechanical Properties of High Strength and Toughness Ship Plate Steel

Studying on Alloying Elements, Phases, Microstructure and Texture in FH36 Ship Plate Steel

TMCP of E/F grade high-strength ship plates in Shougang Co.

Cross section microstructure and homogeneity of mechanical properties of as quenched high strength ship steel

Effect of Heat Treatment on Microstructure and Mechanical Properties of EH36 Alloy

Relationship between Microstructure and Mechanical Properties of V-N Microalloyed High Strength Ship Plate Steel

Effect of alloy elements on microstructure and properties of EH36 steel joint by FAB submerged arc welding

Medium-thickness ship plate steel with ultrahigh intensity and low-temperature impact toughness and manufacturing method thereof

Experimental and numerical study of residual ultimate strength of hull plate subjected to coupled damage of pitting corrosion and crack

Mechanical Properties and Microstructure Transformation Behavior for Welded Joints in Ship Plate Steel with High-Heat Input Welding

Strengthening of Cracked DH36 Steel Plates by CFRP Sheets under Fatigue Loading at Low Temperatures

Microstructure and Mechanical Properties of an Underwater Wet Welded Dissimilar Ferritic/Austenitic Steel Joint

Thickness Dependence of Toughness in Ultra-Heavy Low-Alloyed Steel Plate after Quenching and Tempering

Effects of microstructure and specimen size on the fracture toughness of EH47 shipbuilding steel at low temperature

Performance Study of Copper-Bearing High Strength Ship-Hull Steel

Microstructure and mechanical properties of ASTM A131 EH36 steel fabricated by laser aided additive manufacturing

Comparative study on ductile fracture prediction of high-tensile strength marine structural steels

Effect Of Ce On Rolling Microstructure And Tensile Properties Of Fh40 Shipbuilding Steel Plate

High strength-toughness combination of a low-carbon medium-manganese steel plate with laminated microstructure and retained austenite

A Comparison Study on the Strengthening and Toughening Mechanism between Cu-Bearing Age-Hardening Steel and NiCrMoV Steel

Variations in microstructure and mechanical properties along thickness direction in a heavy high strength low alloy steel plate