Abstract:Pitting corrosion is commonly induced in aging ships and marine structures accompanied by fatigue cracks which may be propagated under cyclic loads. The occurrence of these damages contributes to the performance deterioration of ship structures. From the perspective of safety design, it is of great engineering significance to address the residual ultimate strength of the hull plate with coupled damage of pitting corrosion and crack. In this paper, a compression test was conducted for the hull plate to measure the impact of coupled damage on the ultimate strength. An adaptive fixture is carefully designed which can simulate the boundary conditions of plates supported by real stiffeners. Additionally, the mechanical properties of AH36 steel material are determined using a tensile test. Afterward, the ultimate strength results obtained experimentally are used to verify the reliability of those achieved via nonlinear finite element analysis. Based on the basic behavior under monotonic load, a parametric study is undertaken numerically for the hull plate under cyclic load accounting for the influences of accumulative plastic damage, pitting corrosion and crack. Some interesting findings concerning the structural behavior are presented. It is found that the strength degenerates as the corrosion and crack become more serious or the cycle number increases. The influence mechanism of the plastic damage due to the cyclic load is consistent for the plates with different degrees of corrosion and crack. On the basis of 650 datasets by numerical analysis, an accurate empirical formula is proposed for predicting the residual strength of hull plate with coupled damage under cyclic load by using artificial neural networks.

Experimental and numerical study of residual ultimate strength of hull plate subjected to coupled damage of pitting corrosion and crack

Effect Of Corroded Surface Morphology On Ultra-Low Cycle Fatigue Of Steel Bridge Piers

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

A study on residual ultimate strength of steel unstiffened plate with a crack

Experimental study on the mechanical properties and ultimate strength of accelerated corrosion on hull plates

Numerical investigation on the ultimate strength behaviour and assessment of continuous hull plate under combined biaxial cyclic loads and lateral pressure

Experimental study of low-cycle fatigue crack propagation in hull stiffened plates with symmetric and asymmetric cracks

Progressive collapse analysis and ultimate strength estimation of continuous stiffened panel under longitudinal extreme cyclic load and lateral pressure

Research on Accumulative Plastic Damage for Low-Cycle Fatigue Analysis of Hull Notched Plate

Effect of Corrosion-Induced Structural Degradation on the Ultimate Strength of a High-Tensile-Steel Ship Hull

Experimental study on the fatigue failure mechanism of key joints in deepwater semi-submersible platform structures

A Simple Empirical Formula for Predicting the Ultimate Strength of Ship Plates with Elastically Restrained Edges in Axial Compression

Micromechanics-based Progressive Failure Analysis of Carbon FIber/epoxy Composite Vessel under Combined Internal Pressure and Thermomechanical Loading

Comparative study on ductile fracture prediction of high-tensile strength marine structural steels

Effect of initial geometric imperfections on dynamic ultimate strength of stiffened plate under axial compression for ship structures

Experimental investigation on monitoring the evolution of fatigue microcracks in marine high-strength steel by nonlinear ultrasonic technique

Advanced empirical formulae for the ultimate strength assessment of continuous hull plate under combined biaxial compression and lateral pressure

Experimental Study on Low-Cycle Fatigue Characteristics of Marine Structural Steel

Ultimate Longitudinal Strength of Composite Ship Hulls

Parametric study of buckling and post-buckling behavior for an aluminum hull structure of a high-aspect-ratio twin hull vessel

Reliability Analysis of Ship Hull Girders Considering the Degradations of Corrosion and Fatigue