Toughening Mechanism of Large Heat Input Weld Metal for Marine Engineering Extra-Thick Plate

Junjie Leng,Xinjie Di,Chengning Li,Shanghua Cheng

DOI: https://doi.org/10.1007/s12204-023-2638-3

2023-08-24

Shanghai Jiaotong Daxue Xuebao/Journal of Shanghai Jiaotong University

Abstract:In order to study the latest designed large heat input welding material of marine engineering extra-thick plate, EH36 steel was joined by using twin-wire submerged arc welding with heat inputs of 85, 100 and 115 kJ/cm separately. Meanwhile, the microstructure and mechanical properties were evaluated to explore the toughening mechanism of weld metal. Results show that a lot of active inclusions are obtained in the weld metal due to the design idea of low carbon and oxide metallurgy, which contributes to the generation of numerous fine and interlocking acicular ferrite. The acicular ferrite volume ratio of weld metal exceeds 60%. Moreover, the impact energy at −40 °C surpasses 115 J and the crack tip opening displacement value at −10 °Cis morethan 0.2 mm under three heat inputs owing to the role of acicular ferrite, of which 85 kJ/cm is the best. The martensite-austenite constituents are minor in size and the microstructure of the weld metal in reheated zone is dominated by small massive equiaxed ferrite, without impairing the toughness. As the heat input increases, the content of acicular ferrite drops and then rises; the impact toughness and fracture toughness first worsen consequently and then stabilize on account of the dramatic expansion of the proeutectoid ferrite size.