Burnishing-Induced Ultra-Fine Grained Pure Iron Surface Layer and Its Corrosion Resistance

Ning Li,Wei Xia,Jing Zhao,Feng-lei Li

DOI: https://doi.org/10.3969/j.issn.1000-565X.2014.09.001

2014-01-01

Abstract:In the investigation,by means of a new surface self-nanocrystallization technique named SPRB (Severe Plasticity Roller Burnishing),a gradient ultra-fine grain (UFG)surface layer of a minimum grain size of about 300nm was fabricated on pure iron.Then,the microstructure and the corrosion behavior of UFG surface layer were analyzed by means of TEM,XRD,SEMand electrochemical methods.The results show that (1)the outermost layer hardness of UFG iron is improved by more than 1.6 times in comparison with that of coarse grain (CG)iron;(2)a strongly basal-textured grain orientation forms on the UFG surface and its micro strain is (0.313 ±0.017)%;(3)in 3.5% NaCl solution,the open circuit corrosion potential of UFG Fe is 24 mV more than that of CG Fe in the positive direction,and the corrosion current density decreases from 2.371 ×10 -5 A /cm2 of CG Fe to 7.547 ×10 -8 A /cm2 of UFG Fe;(4)in 6% FeCl3 solution,the pitting rate of UFG Fe is about half as much as that of CG Fe;(5)the corrosion resistance of UFG Fe is remarkably improved in comparison with that of CG Fe;and (6)the corrosion re-sistance improvement of UFG Fe is attributed to the surface grain refinement and the formation of the strongly basal-textured grain orientation.