Abstract:This article sought to determine the response of a carbon foam material derived from polyurethane foam when subjected to a quasi-static compression load. The effects of the foam pore densities and additives (solvents) on the compression strength, compressive modulus, and surface morphology of the carbon foam were investigated. In this study, three different carbon foam pore densities (20, 40, and 60 ppi) and three solvents for the phenol–formaldehyde resins that coated the polymer foam (acetone, ethanol, and methanol) were used. Carbon foams were derived from polyurethane foams by carbonization. Quasi-static compression testing was carried out using a universal testing machine. The compressive strength, compressive modulus, and relative density of these different carbon foams were computed and compared. Two-way ANOVA analyses were performed to compare the significance of solvents and pore density. These results showed that pore density and solvents significantly affected the compressive strength, compressive modulus, and surface morphology of the fabricated polyurethane-derived carbon foam. Finally, the maximum compressive strength and maximum compressive modulus were observed in carbon foam (60 ppi) with 40% methanol as the solvent. Conversely, a minimum compressive strength was observed for a 20 ppi carbon foam with a 20% acetone solvent, and a minimum compressive modulus was observed for a 20 ppi foam with 40% methanol. Lastly, the chemical composition of the polyurethane foams was investigated, and these results indicated that the polyurethane-derived carbon foam had 96% carbon atoms after carbonization.

Effect of Physical and Chemical Properties of Phenol-Formaldehyde Resin on Its Foaming Behaviors

Effects of Heating Rate on the Foaming Behavior and Pore Structure of Carbon Foams Derived from Phenol-Formaldehyde Resin

Silicone-modified Phenolic Resin: Relationships Between Molecular Structure and Curing Behavior

Preparation of glass fiber reinforced phenolic injection molding materials and its properties

Study of Post-curing Properties of Wood Flour Reinforced Phenolic Molding Materials

Effects of Phenolic Resin on the Foaming Behavior and Biofilm Biomass of High Softening Point Pitch

Effect of Pre-Curing Process on Epoxy Resin Foaming Using Carbon Dioxide As Blowing Agent

Preparation and Characterization of Porous Carbons Obtained from Mixtures of Furfuryl Alcohol and Phenol-Formaldehyde Resin

Investigating the hydrophilicity of phenol formaldehyde foams: Effects of synthesis parameters

Preparation and Characterization of Carbon Foams Derived from Aluminosilicate and Phenolic Resin

Preparation and properties of phenolic foam modified with boric acid and organosiloxane by supercritical CO2 technology

The Property of A Novel Crosslinked Foam from Thermoplastic Phenol‐Terminated Polyphenylene Ether Resin with High Molecular Weight (MPF) Cured by Hydroxymethylated Phenol‐Terminated Polyphenylene Ether Resin with Low Molecular Weight (LPR)

Preparation of epoxy resin foam by composite foaming agent prepared from microporous silica and 4,4 '-bisoxybenzenesulfonyl hydrazide

Experimental Analysis of the Mechanical Properties of Carbon Foams Under Quasi-Static Compressive Loads

Effect of the Aromatic Amine Curing Agent Structure on Properties of Epoxy Resin-Based Syntactic Foams

Effect of Final Pyrolysis Temperature on the Mechanical and Thermal Properties of Carbon Foams Reinforced by Aluminosilicate

Facile Synthesis of Formaldehyde-Free Bio-Based Thermoset Resins for Fabrication of Highly Efficient Foams

Design and Preparation of Shape Memory Phenol–formaldehyde Foam Composites with Excellent Thermal Stability and Mechanical Properties

Study of preparation and properties of environmentally friendly phenolic resin for mining

Preparation of Bisphenol A Polyaryl Ether Nitrile Microporous Foam

Effects of coal characteristics on the structure and performance of coal-based carbon foam prepared by self-foaming technique under atmospheric pressure