Abstract:In this study, polyolefin elastomer (POE) foams were prepared without any curing agent using a single-step foaming technique. The effect of azodicarbonamide (ADC) content as a chemical foaming agent on the foams' morphology and mechanical properties was studied using scanning electron microscopy (SEM), mechanical properties (tension and compression) and hardness. The results showed that increasing the ADC content from 2 to 3, 4 and 5 phr (parts per hundred rubber) decreased the foam density from 0.75 to 0.71, 0.65 and 0.61 g/cm3, respectively. The morphological analysis revealed that increasing the ADC content from 2 to 4 phr produced smaller cell sizes from 153 to 109 μm (29% lower), but a higher cell density from 103 to 591 cells/mm3 (470% higher). However, using 5 phr of ADC led to a larger cell size (148 μm) and lower cell density (483 cells/mm3) due to cell coalescence. The tensile modulus, strength at break, elongation and hardness properties continuously decreased by 28%, 21%, 16% and 14%, respectively, with increasing ADC content (2 to 5 phr). On the other hand, the compressive properties, including elastic modulus and compressive strength, increased by 20% and 64%, respectively, with increasing ADC content (2 to 5 phr). The tensile and compression tests revealed that the former is more dependent on foam density (foaming ratio), while the latter is mainly controlled by the cellular structure (cell size, cell density and internal gas pressure). In addition, 2D SEM images were used to simulate the foams' real 3D structure, which was used in finite element methods (FEM) to simulate the stress–strain behavior of the samples at two levels: micro-scale and macro-scale. Finally, the FEM results were compared to the experimental data. Based on the information obtained, a good agreement between the macro-scale stress–strain behavior generated by the FEM simulations and experimental data was obtained. While the FEM results showed that the sample with 3 phr of ADC had the lowest micro-scale stress, the sample with 5 phr had the highest micro-scale stress due to smaller and larger cell sizes, respectively.

Preparation of epoxy resin foam by composite foaming agent prepared from microporous silica and 4,4 '-bisoxybenzenesulfonyl hydrazide

Synthesis and properties of an epoxy resin containing trifluoromethyl side chains and its cross-linking networks with different curing agents

Effect of the Aromatic Amine Curing Agent Structure on Properties of Epoxy Resin-Based Syntactic Foams

Cell Characteristics of Epoxy Resin Foamed by Step Temperature-Rising Process Using Supercritical Carbon Dioxide As Blowing Agent

Preparation and Tensile-compressive Properties of Syntactic Foams of Epoxy Resin Filled with Fly Ash Cenospheres

Research on Properties of Epoxy Resin/Hollow Glass Microspheres Foam Materials

Effect of Pre-Curing Process on Epoxy Resin Foaming Using Carbon Dioxide As Blowing Agent

Effects of silane coupling agent modifications of hollow glass microspheres on syntactic foams with epoxy matrix

Effects of reactive diluent on processing, structure, and properties of epoxy foams and their sandwich composites

Synergetic Effect Between Curing Reaction and CO2 Diffusion for Microcellular Epoxy Foam Preparation in Supercritical CO2

New Insights on Expandability of Pre-Cured Epoxy Using a Solid-State CO2-Foaming Technique

Effect of Physical and Chemical Properties of Phenol-Formaldehyde Resin on Its Foaming Behaviors

The relationship between cellular microstructure and the mechanical properties of styrene/methyl methacrylate copolymer‐silica nanocomposite foams prepared by a supercritical CO2 blowing agent

Rational Design of High‐performance Epoxy/expandable Microsphere Foam with Outstanding Mechanical, Thermal, and Dielectric Properties

Preparation, Characterization, and Mechanical Properties of Microcellular Poly(Aryl Ether Ketone) Foams

Synthesis of a Bio-Based and Intrinsically Anti-Flammable Epoxy Thermoset and the Application of Its Carbonized Foam As an Efficient CO2 Capture Adsorbent

Study on the foaming behavior of density‐controllable epoxy resin composite foam under negative pressure environment

Diatomite‐filled epoxy resin composites: Curing behavior, dielectric, and thermal properties

Lightweight epoxy foams prepared with arranged hollow-glass-microspheres/epoxy hollow spheres

Experimental and Finite Element Simulation of Polyolefin Elastomer Foams Using Real 3D Structures: Effect of Foaming Agent Content

Preparation and Mechanical Properties of Carbon Fiber Reinforced Multiphase Epoxy Syntactic Foam (Cf-R-epoxy/hgms/cfr-hems Foam)