Abstract:The terpolymer latex of methyl methacrylate (MMA)/butyl acrylate (BA)/dimethylaminoethyl methacrylate (DMAEMA) was prepared by batch and semi-continuous emulsion copolymerization. The effects of emulsifier type and concentration, polymerization temperature, and feed policy of emulsified monomers on process stability of the copolymerization and properties of the terpolymer latex were studied systematically. The results suggest that the selection of emulsifier should not be based on the HLB values for the DMAEMA-containing systems. The co-emulsifiers suitable for stabilizing the copolymerization process are in the order of SDS/OP>SDBS/OP>OT/OP. The results also indicate that an increase in amount of the co-emulsifiers, sodium dodecyl sulfate (SDS) and octyl phenol polyoxyethyl ether (OP), improves the process stability, decreases the surface tension and particle size of latices; however, it has little influence on the electrolyte stability when SDS/OP ratio is unchanged. A decrease in reaction temperature improves the process stability of polymerization but decreases the electrolyte stability of latices. The DMAEMA content does not affect the process stability significantly under investigated conditions but contributes to improve the electrolyte stability of latices. Compared to the batch polymerization process, the semi-continuous polymerization with a lower monomer feed rate provides better process stability for the polymerization and better electrolyte stability for the latices.

Study on polymerizable microemulsion systems containing methyl methacrylate

Emulsion polymerization of methyl methacrylate in concentration of emulsifiers below their CMCs—polymerization rate, particle size, and particle-size distribution

Stability of Emulsion Copolymerization of Acrylic Monomers Containing Amino and Hydroxyl Groups

Preparation and Characterization of MMA-BA-DMAEMA Terpolymer Latex

Reversible addition–fragmentation chain transfer polymerization of methyl methacrylate in emulsion

Preparation of Bicontinuous Porous Polymeric Materials Via Microemulsion Polymerization

Study on nano-size PMMA particles prepared by O/W microemulsion polymerization. - (1) Phase diagram, compatibilization and reaction kinetics

The effect of monomer polarity on MMA/BA/ Sodium methacrylate emulsifier-free emulsion copolymerization

Study of Kinetic of Emulsion Copolymerization of Methyl Methacrylate/ethyl Acrylate

Research of Styrene/Aerylonitrille/N-Phenlymaleimide Emalsion Copolymerization

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

Kinetics of Suspended Emulsion Polymerization of Methyl Methacrylate

Electrostatic Absorption of Initiator Onto Nanometer SiO2 Particles and In-Situ Emulsion Polymerization of Methyl Methacrylate in the Presence of Modified Nanometer SiO2

Effects of Monomer Polarity on Mma/Ba/Nama Emulsifier-Free Emulsion Copolymerization

STUDY ON NANO-SIZE PMMA PARTICLES PREPARED BY O/W MICROEMULSION POLYMERIZATION --(Ⅰ) PHASE DIAGRAM, COMPATIBILIZATION AND REACTION KINETICS

Particle Features of A Poly(Methyl Methacrylate) Resin Prepared by A New Emulsion Polymerization Process

SURFACTANT-FREE EMULSION POLYMERIZATION OF METHYL METHACRYLATE INITIATED BY Α-Methyl STYRENE-MALEIC ANHYDRIDE COPOLYMER MACROINITIATOR

Emulsion Polymerization of Mma/Ba in the Presence of Ionic Surface Active Monomers (I) - Syntheses and Polymerization Reactivities of the Surfmers

Comparison of RAFT Ab Initio Emulsion Polymerization of Methyl Methacrylate and Styrene Mediated by Oligo(methacrylic Acid‐b‐methyl Methacrylate) Trithiocarbonate Surfactant

Stability Of Emulsifier-Free Emulsion Copolymerization Of Methyl Methacrylate/Butyl Acrylate/Sodium Mono(Ethyl Polyoxyethylene)Maleate

Kinetics of Styrene-Methyl Methacrylate Suspension-Emulsion Combined Polymerization