Abstract:This brief paper reported an Ag/Al₂O₃ catalyst of high catalytic performance in C₃H6-SCR (selective catalytic reduction with C₃H6 as the reducer), and demonstrated a new strategy for the preparation of high active Ag/Al₂O₃ catalyst by the coupling co-precipitation and impregnation method. The results show that the coupling co-precipitation and impregnation catalyst was higher active than the usual impregnated catalyst in C₃H6-SCR of NO with broad active temperature window (420-600 °C), and the highest conversions of NO achieved 91% over the coupling co-precipitation and impregnation catalyst at 500 °C. The porous structure parameter, crystal phase structure, surface acidity property and particle morphology of the Ag/Al₂O₃ catalyst were characterized by the Brunauer-Emmett-Teller (BET) method, X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV-vis spectra and temperature programmed desorption of ammonia (NH₃-TPD), respectively. Based on the characterization, it is found that the catalyst prepared by the coupling co-precipitation and impregnation method has smaller particles and better dispersion than the usual impregnated catalyst, and so the catalyst exhibited excellent catalytic activity. NH₃-TPD results illustrate that the weak and medium-strong acid sites is conducive to the reactivity of catalyst.

Selective Catalytic Reduction of NO with C3H6 over SnO2-Al2O3 Binary Metal Oxide Catalysts

The Activity and Characterization of Sol-Gel Sn/Al2o3 Catalyst for Selective Catalytic Reduction of Nox in the Presence of Oxygen

MnOx-SnO2 Catalysts Synthesized by a Redox Coprecipitation Method for Selective Catalytic Reduction of NO by NH3

Selective Catalytic Reduction of NOx with Propene over SnO2/Al2O3 Catalyst

Selective catalytic reduction of NO by C3H8 over CoOx/Al2O3: An investigation of structure–activity relationships

Ce-Sn Binary Oxide Catalyst for the Selective Catalytic Reduction of NOx by NH3

Selective catalytic reduction of NO over metal oxide or noble metal-doped In 2 O 3 /Al 2 O 3 catalysts by propene in the presence of oxygen

Cooperation of Ag/Al2O3 and Sn/Al2O3 Catalysts for the Selective Reduction of NO by Propene

The activity and characterization of MnOx–CeO2–ZrO2/γ-Al2O3 catalysts for low temperature selective catalytic reduction of NO with NH3

Sn-doped TiO2 Supporting V2O5 Catalyst for Selective Catalytic Reduction of Nitric Oxide by Ammonia

CuO/Sn_(0.8)Ti_(0.2)O_2 Catalyst: Characterization and Catalytic Performance in NO+CO Reaction

Interaction Between Nickel Oxide and Support Promotes Selective Catalytic Reduction of NOx with C3H6

Study on the surface properties of TiO2-SnO2 supported catalysts for low temperature selective catalytic reduction of NOx

Interaction between Nickel Oxide and Support Promotes Selective Catalytic Reduction of NOx with C3 H6

Sn-X Ti1-X O-2 Solid Solution Catalysts for Nitrogen Oxide Selective Catalytic Reduction by Propene in Presence of Oxygen

Lean NOx reduction over Sn1−xZrxO2 solid solutions

Cr–MnO Mixed-Oxide Catalysts for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Low-temperature Selective Catalytic Reduction of NO with NH3 over Monolith Catalyst of MnOx/CeO2–ZrO2–Al2O3

High Activity Sno2/Al2o3 Catalyst For No Reduction In The Presence Of Oxygen

Preparation of the Coupling Co-Precipitation and Impregnation Catalyst Ag/Al₂O₃ with High Catalytic Performance in Selective Catalytic Reduction of NO with C₃H6.

Interaction between Nickel Oxide and Support Promotes Selective Catalytic Reduction of NO <sub> <i>x</i> </sub> with C <sub>3</sub> H <sub>6</sub>