Abstract:Poly(butylene succinate) (PBS) is regarded as one of the most promising biodegradable polymers due to the excellent mechanical properties,thermal stability,and thermo-process.However,due to its low melt viscosity,PBS microcellular foam is difficult to fabricate by using supercritical CO2 foaming.To improve its viscoelasticity and foamability,PBS was modified through ionizing in this paper.The segmented PBS urethane ionenes (PBSUI)containing secondary amine cation were synthesized by chain extension reaction of dihydroxyl terminated poly (butylene succinate) and diethanolamine hydrochloride (DEAH) in the presence of hexamethylene diisocyanate (HDI).Then the PBSUI foams were fabricated by supercritical CO2 in a rapid depressururization process via batch foaming method.Rotational rheometer and XRD were used to characterize the rheological and crystalline properties of PBSUI.The results reveal that the melt viscosity and relaxation time of PBSUI increase with rise of the urethane ionic group content,while both the crystallinity and spherulitic diameter of foaming PBSUI and unfoaming PBSUI decrease.The results of SEM demonstrate that the foam shape of PBSUI transforms from circle into polygon with increasing the urethane ionic group content.Moreover,both the cell density and expansion volume ratio increase,while the average cell diameter,the cell wall thickness and the cell opening ratio decrease when the urethane ionic group content increases from 1％ to 5 ％.PBSUI foam with 3 ％ urethane ionic group could achieve micro cell,the average cell diameter is 2.05μm,the cell density is 1.73 × 1010 cm-3 and the expansion volume ratio is more than 10.The results illuminate that when urethane ionic group is introduced into PBS,and PBSU microcellular foam is successfully prepared by supercritical carbon dioxide.The reason is attributed to physical crosslinking and heterogeneous nucleation effect caused by ion clusters aggregation,and the PBSU foaming performance is significantly improved.

Foam Properties of Poly(buytlene succinate) Ionomers

Study on the Foaming Behaviors of PBS and its Modification with PA6IcoT Assisted by scCO2

Mechanical and thermal properties of poly(butylene succinate)/plant fiber biodegradable composite

High Molecular Weight Poly(butylene Succinate-Co-furandicarboxylate) with 10 Mol% of BF Unit: Synthesis, Crystallization-Melting Behavior and Mechanical Properties

Fractionated Crystallization, Polymorphic Crystalline Structure, and Spherulite Morphology of Poly(butylene Adipate) in Its Miscible Blend with Poly(butylene Succinate)

Preparation of Enhanced Poly(Butylene Succinate) Foams

Rheological Properties and Foam Preparation of Biodegradable Poly(butylene Succinate)

Mechanical, Crystallization, Rheological, and Supercritical CO2 Foaming Properties of Polybutylene Succinate Nanocomposites: Impact of Carbon Nanofiber Content

Study on the Foaming Behaviors of PBS and Its Modification with PA6IcoT Assisted by scCO 2

Engineering of Polybutylene Succinate with Long-Chain Branching Toward High Foamability and Degradation

Effect of Poly(butylenes Succinate) on Poly(lactic Acid) Foaming Behavior: Formation of Open Cell Structure

Low-shrinkage Biodegradable PBST/PBS Foams Fabricated by Microcellular Foaming Using CO2 & N2 As Co-Blowing Agents

Effect of Crosslinking Agent and Branching Agent on Morphological and Physical Properties of Poly(Butylene succinate) Foams

Effect of Processing Conditions on Poly(butylene Succinate) Foam Materials

A green and efficient synthetic strategy for the preparation of PBS ionomers with high molecular weight, high ionic group content and good combined properties

Review on poly (butylene succinate) foams: Modifications, foaming behaviors and applications

Adsorption characteristics of amphiphilic open-cell poly(butylene succinate) foams with ultrahigh porosity

The Essential Role of PBS on PBAT Foaming under Supercritical CO2 Toward Green Engineering

Fully Biodegradable Blends of Poly(butylene Succinate) and Poly(butylene Carbonate): Miscibility, Thermal Properties, Crystallization Behavior and Mechanical Properties

Synthesis and Characterization of Biodegradable Poly(butylene Succinate‐co‐propylene Succinate)s

Synthesis and Properties of Biodegradable Poly(butylene succinate-co-butylene 2,2-dimethyl succinate)