Abstract:This work attempts to prepare ethylene-a-olefin copolymer with relatively narrow composition distribution by modification of TiCl4/MgCl2 type supported Ziegler-Natta catalyst. A TiCl4/ID/MgCl2 type catalyst, where ID is a diester, was treated at room temperature with 2,6-'Pr2C6H3-OH at phenol: Ti molar ratio of 1:1 and the modified catalyst was analyzed for contents of titanium and aryloxy group. It was found that about one third of the titanium atoms in the modified catalyst (M-cat) was connected with an aryloxy group, but its Ti content was decreased to 1.44 wt% from 2.36 wt% of the original catalyst (O-cat). Ethylene-1-hexene copolymerization was conducted in n-heptane with M-cat or O-cat as catalyst and triisobutyl aluminium or methylaluminoxane as cocatalyst. The M-cat showed similar activity as the O-cat in catalyzing the copolymerization, but presented a weaker comonomer activation effect than the latter. The 1-hexene content of copolymer synthesized by M-cat was lower than that of the product of O-cat at the same conditions, but had a markedly narrower composition distribution. Each copolymer sample was fractionated into two fractions by extraction with boiling n-heptane, and the soluble part contains much more 1-hexene units than the insoluble part. The ratio of I-hexene content in the soluble fraction to that of the insoluble fraction was higher than 18 in copolymer prepared with O-cat, but this ratio was reduced to 3.7 when M-cat was used as the catalyst. On the other hand, the soluble part of copolymer prepared with M-cat showed a more random sequence distribution than that of the O-cat. The distributions of active centers in both the M-cat and O-cat were studied by deconvolution of the polymer's molecular weight distribution curves with multiple Flory most-probable distribution function. Both catalysts showed a broad molecular weight distribution that can be ascribed to 5 similar to 6 types of active centers, but the introduction of aryloxy group in the catalyst caused marked changes in the active center distribution. Possible mechanism of the catalyst modification was proposed.

The Investigation of Terpolymerization of Ethylene/propylene/ω-Cl-α-vinyl Monomers Catalyzed by Cat.L-Pd Catalyst

ETHYLENE POLYMERIZATION WITH CORE-SHELL ZIEGLER-NATTA HYBRID CATALYSTS

Ethylene polymerization with metallocene/late transition metal combined catalysts

Advanced Catalyst Technology for Broad/Bimodal Polyethylene, Achieved by Polymer-Coated Particles Supporting Hybrid Catalyst

Effect of Catalysts Supporting on Tandem Polymerization of Ethylene Stock in Synthesis of Ethylene-1-Hexene Copolymer

Investigation on Terpolymer of Ethylene/propylene/ω-Bromo-α-olefins Catalyzed by Titanium Complexes

Synthesis of Polyethylene-G-polydimethylsiloxane Graft Copolymers by Copolymerization of Ethylene with Polydimethylsiloxane Macromonomer

(Co)polymerization of Ethylene Via Nonmetallocene Catalysts with Diphenyl Phosphoroso Schiff‐base Ligand

Studies on Vocl3/Mgcl2/Nay/Al(2)Et(3)Cl(3) Complex Support Catalysts for the Copolymerization of Ethylene and Propylene

Study on preparation of polyolefins over complex support catalysts I. Preparation of ethylene-propylene copolymer over VOCl3/MgCl2/NaY ( SiO2)

The Investigation of Novel Non‐metallocene Catalysts with Phenoxy‐imine Ligands for Ethylene (Co‐)polymerization

Efficient Copolymerization of Ethylene with Polar Divinyl Monomer by Phosphino‐Phenolate Nickel Catalyst

Propylene Polymerization to High Molecular Weight Atactic Polypropylene and Copolymerization with 1-Hexene Using Monocyclopentadienyl Titanium Catalysts.

Exploring steric effect of electron-donating group in palladium and nickel mediated ethylene polymerization and copolymerization with polar monomers

Synthesis and performance of olefin copolymers produced with monocyclopentadienyl titanium phosphinimide complex as viscosity modifiers

Studies on Synthesis of Low Isotactic Polypropylene by Using a Novel MgCl2-supported and Low Ti-loading Catalyst

Copolymerization of Propylene and Long-Chain Unsaturated Aromatic Esters with Big Steric Hindrance over TiCl4/MgCl2/AlEt3

Aqueous Coordination‐Insertion Copolymerization for Producing High Molecular Weight Polar Polyolefins

Ethylene-1-Hexene Copolymerization with A 2,6-Diisopropylphenol Modified Supported Ziegler-Natta Catalyst

With different structure ligands heterogeneous Ziegler–Natta catalysts for the preparation of copolymer of ethylene and 1-octene with high comonomer incorporation

The Third Compound Promoted Copolymerization of Ethylene with 4‐Penten‐1‐ol by Using Metallocene Catalyst