Abstract:This work attempts to prepare ethylene-a-olefin copolymer with relatively narrow composition distribution by modification of TiCl4/MgCl2 type supported Ziegler-Natta catalyst. A TiCl4/ID/MgCl2 type catalyst, where ID is a diester, was treated at room temperature with 2,6-'Pr2C6H3-OH at phenol: Ti molar ratio of 1:1 and the modified catalyst was analyzed for contents of titanium and aryloxy group. It was found that about one third of the titanium atoms in the modified catalyst (M-cat) was connected with an aryloxy group, but its Ti content was decreased to 1.44 wt% from 2.36 wt% of the original catalyst (O-cat). Ethylene-1-hexene copolymerization was conducted in n-heptane with M-cat or O-cat as catalyst and triisobutyl aluminium or methylaluminoxane as cocatalyst. The M-cat showed similar activity as the O-cat in catalyzing the copolymerization, but presented a weaker comonomer activation effect than the latter. The 1-hexene content of copolymer synthesized by M-cat was lower than that of the product of O-cat at the same conditions, but had a markedly narrower composition distribution. Each copolymer sample was fractionated into two fractions by extraction with boiling n-heptane, and the soluble part contains much more 1-hexene units than the insoluble part. The ratio of I-hexene content in the soluble fraction to that of the insoluble fraction was higher than 18 in copolymer prepared with O-cat, but this ratio was reduced to 3.7 when M-cat was used as the catalyst. On the other hand, the soluble part of copolymer prepared with M-cat showed a more random sequence distribution than that of the O-cat. The distributions of active centers in both the M-cat and O-cat were studied by deconvolution of the polymer's molecular weight distribution curves with multiple Flory most-probable distribution function. Both catalysts showed a broad molecular weight distribution that can be ascribed to 5 similar to 6 types of active centers, but the introduction of aryloxy group in the catalyst caused marked changes in the active center distribution. Possible mechanism of the catalyst modification was proposed.

Copolymerization of Propylene and Long-Chain Unsaturated Aromatic Esters with Big Steric Hindrance over TiCl4/MgCl2/AlEt3

Effects of Precomplexation on Activity of TiCl4/SiO2-MgCl2Catalyst in Propylene Polymerization and Polymer Particle Morphology

TiCl4 Immobilized on a Composite Support SiO2/MgCl2·x(1,4‐butanediol)/poly[styrene‐co‐(acrylic Acid)] for Ethylene Polymerization: the Barrier Effect of Poly[styrene‐co‐(acrylic Acid)]

Effect of Catalysts Supporting on Tandem Polymerization of Ethylene Stock in Synthesis of Ethylene-1-Hexene Copolymer

Synthesis of Ultrahigh-Molecular-weight Ethylene-1-hexene Copolymers with High Hexene Content Via Living Polymerization with Fluorinated Bis(phenoxy-Imine) Titanium(iv).

COMPOSITION AND TACTICITY DISTRIBUTION OF PROPYLENE BUTENE COPOLYMER

COPOLYMERIZATION OF PROPENE WITH 1-ALKENES USING A MGCL2/TICL4 CATALYST

Copolymerization of propene with high‐1‐olefin using a MgCl2/TiCl4 catalyst

Copolymerization of Propene with 1‐alkenes Using a MgCl2/TiCl4 Catalyst

Supported Catalyst Without External Electron Donor for Propylene Polymerization Ii. Tacticity Distribution and Microstructure of Polypropylene

Nonconjugated α,ω-Diolefin/Propylene Copolymerization to Long Chain-Branched Polypropylene by Ziegler–Natta Catalyst: Overcoming Steric Hindrance by Introducing an Extra Electronic Pulling Effect

Influence of polymerization conditions on the chain structure of ethylene-propylene copolymer prepared by MgCl_2/TiCl_4 catalyst

Highly active Ziegler-Natta Catalysts for propylene polymerization (2) effects of Al/Ti ratio and polymerization temperature

Ethylene/1-Octadecene Copolymerization Using [Eta(5):Eta(1)-C5me4-4-R-1-6-R-C6h2o]Ticl2 Catalysts

Studies on Synthesis of Low Isotactic Polypropylene by Using a Novel MgCl2-supported and Low Ti-loading Catalyst

The Investigation of Terpolymerization of Ethylene/propylene/ω-Cl-α-vinyl Monomers Catalyzed by Cat.L-Pd Catalyst

Synthesis of Ethylene Copolymers with 2-Allylphenol by Half-Titanocene Catalysts Containing SiEt3-, SiiPr3-Substituted Phenoxide ligands, Cp*TiCl2(O-2,6-iPr2-4-SiR3-C6H2) (R = Et, iPr)

Ethylene-1-Hexene Copolymerization with A 2,6-Diisopropylphenol Modified Supported Ziegler-Natta Catalyst

Ethylene–propylene Copolymerization with Bis(β‐enaminoketonato) Titanium Complexes Activated with Modified Methylaluminoxane

Enhancing Stereoselectivity of Propylene Polymerization with MgCl2-supported Ziegler-Natta Catalysts by Electron Donor: Strong Effects of Titanium Dispersion State

Propylene Polymerization to High Molecular Weight Atactic Polypropylene and Copolymerization with 1-Hexene Using Monocyclopentadienyl Titanium Catalysts.