Abstract:Highly porous microcellular SiC ceramics, a kind of biomorphic SiC with anisotropic pore structures, were prepared by reactive infiltration of Si vapor into porous carbon templates produced from basswood by high-temperature pyrolysis. The phase identification and morphology of the carbon templates and porous microcellular SiC ceramics were investigated by X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. The macroscopical properties of the resulting biomorphic SiC ceramics were characterized by pore size distribution, open porosity and bending strength. The process of the reactive infiltration of Si vapor into basswood carbon template was also introduced and analyzed. The SiC ceramics possessed a unique pore microstructure pseudomorphous to basswood charcoal. The SiC ceramics were composed of major crystal phase of β-SiC and secondary phase of unreacted carbon, and of a multimodal pore size distribution. Si vapor diffused through the primary β-SiC layer, which was reaction rate controlling step of the Si vapor infiltration/reaction process, and reacted with the inner carbon to form β-SiC at the SiC–C interface. The open porosity and bending strength of the porous SiC ceramics were above 50% and 50MPa, respectively.

Preparation and formation mechanism analysis of morph-genetic SiC fiber fabric ceramic

Microstructure analysis of morph-genetic SiC/C ceramics from wood

The fabrication of Al2O3/C morph-genetic ceramics by biotemplating from ramie fibers

Synthesis and Microstructure Analysis of Morphgenetic Materials

Preparation and characterization of SiC porous ceramics from ramie fibers

Effect of biological template modification on pore structure and gas sensitivity properties of SnO2 morph-genetic ceramic

Fabrication of Porous SiC Ceramics with Special Morphologies by Sacrificing Template Method

Preparation and mechanical behaviors of multiscale SiC nanowires/carbon fiber reinforced silicon oxycarbide ceramic composites

Fabrication and Properties of Reaction-Formed SiC by Infiltrating Molten Si into Mesocarbon Microbeads-Based Carbon Preform

Preparation of Complex-Shape SiC Ceramic Composites Parts Derived from Phenolic Resin Template

Microstructure and Properties of Reaction-Formed SiC Ceramic Derived from Mesocarbon Microbeads

Fabrication of Tubular SiC/Si Ceramic Composites by Carbon Template Conversion

Reaction Forming of Silicon Carbide Ceramic Using Phenolic Resin Derived Porous Carbon Preform

Morph-genetic Al2O3 Ceramic Derived from Bio-Templates

Preparation and Properties of Porous Microcellular SiC Ceramics by Reactive Infiltration of Si Vapor into Carbonized Basswood

Preparation of carbon fiber reinforced silicon carbide porous ceramiccomposites with three dimensional network structure

Morphology Design of Porous Si2N2O Ceramics via Silica Poly-Hollow Microspheres

Preparation and R-Curve Properties of Laminated Si/Sic Ceramics from Paper

Pore Morphology Designs of Porous Si3n4-Based Ceramics Using Si3n4 and Al2o3 Poly-Hollow Microspheres As Pore-Forming Agents

Microstructure Evolution Process of Porous Silicon Carbide Ceramics Prepared Through Coat-Mix Method

Tailoring of Porous Structure in Macro-Meso-Microporous SiC Ultrathin Fibers via Electrospinning Combined with Polymer-Derived Ceramics Route