Fabrication of Porous Al2TiO5-Al2O3 Ceramics Using Al2O3 Hollow Spheres Coated with TiO2 Sol
Jialiang Zhao,Jinlian Li,Xiaofang Zhang,Xudong Luo,JiJia Li,Xin Qi,Yiran Man,Rui Lin,Zhipeng Xie
DOI: https://doi.org/10.1016/j.ceramint.2022.05.155
IF: 5.532
2022-01-01
Ceramics International
Abstract:Currently, porous Al2O3 ceramics have attracted extensive attention because of their unique properties. How-ever, the low strength of porous Al2O3 ceramics constrains their practical application. Herein, the porous Al2TiO5-Al(2)O(3 )ceramics with higher strength were prepared through the Al(2)O(3 )hollow spheres (HSs) coated with TiO2 sol using co-precipitation method. The present work is to study the effects of Al(2)TiO(5 )solution content on the sintering behavior and mechanical properties of porous Al(2)O(3 )ceramics. Then, the enhancement mechanism was analyzed by comparison of the bulk density, porous, shrinkage, compressive strength, and the resultant microstructure. With Ti(SO4)(2) solution content as the primary parameter to control the Al(2)TiO(5 )content, it was found that when Ti(SO4)(2) solution content was 15 mL, the minimum value of porosity reached 30.4%, while the maximum values of bulk density and shrinkage reached 2.52 g/cm(3 )and 9.4%, respectively. Furthermore, the compressive strength of porous Al2O3 ceramics containing 15 mL Ti(SO4)(2) solution reached a maximum of 53.1 MPa, which is attributed to the formation of the liquid phase and the presence of elongated Al2TiO5 grains. This results from the improvement of bonding strength between Al(2)O(3 )HSs.