Abstract:TiAl-based alloy have potential as high temperature structural materials for aerospace applications, especially for thermal protection systems in aerospace vehicles including skin materials. Unfortunately, the ductility and formability of TiAl-based alloys are rather poor and thus gamma-TiAl sheets or foils are quite difficult to be manufactured by traditional methods and still far from practical applications. In the present work, commercial pure Ti foils and in-house fabricated TiB2/Al composite foils were alternately stacked and rolled to prepare Ti-(TiB2/Al) laminates, and then heat treatment was utilized to make liquid Al react with solid Ti, and finally TiAl-based composite sheet with multi-layer distributed reinforcement TiB2 particles were achieved. This method avoided the direct deformation of brittle TiAl billets and thus the near-net-shape processing of TiAl-based alloys sheets was feasible. Phase transformation and microstructure evolution during heat treatment were investigated and mechanical properties of the resulting micro-laminated TiB2-TiAl composite sheets were evaluated. The results showed that porous TiAl3 layers were produced by the reaction between liquid Al and solid Ti because of Kirkendall effect, and the following densification treatment under 50 MPa at 1300 degrees C for 2 h significantly improved the relative density of material. Subsequently, the reaction diffusion between TiAl3 and residual Ti proceeded in the following heat treatment, and finally fully lamellar (alpha(2)-Ti3Al+gamma-TiAl) layers were obtained. TiB2 particles did not participate in any reaction and remained, and displayed multi layered distribution in the matrix (alpha(2)-Ti3Al+gamma-TiAl) layers. TiB2 rich layer hindered the coarsening of lamellar colony of (alpha(2)-Ti3Al+gamma-TiAl) layer. Tensile properties at 800 degrees C of multi layered TiB2 TiAl composite sheets remarkably increased because of an increase of energy dissipation caused by plastic deformation.

Preparation And Mechanical Properties Of Large-Sized Tial/Ti3al Microlaminated Thin Sheets

PREPARATION AND PROPERTIES OF TiB2/TiAl COMPOSITE SHEETS WITH LAYERED STRUCTURE

Fabrication of Fully Dense Tial-Based Composite Sheets with A Novel Microlaminated Microstructure

Preparation and Performance of Large-Sized Ti/Ti-Al Microlaminated Composite

Study on Microstructures and Mechanical Properties of Ti/Ti-Al Microlaminated Composite

Microstructure and Mechanical Properties of Ti/Ti-Al Multi-layered Composite Prepared by EB-PVD

TiAl-BASED COMPOSITE SHEET WITH MULTI-LAYER DISTRIBUTED REINFORCEMENT PREPARED BY SOLID-LIQUID REACTION

Fabrication, Microstructure and Properties of Electron Beam-Physical Vapor Deposited Tial Sheet and Tial/Nb Laminated Composites

Tensile behavior and fractography of Ti-TiAl multi-layered foil prepared by electron beam physical vapor deposition technology

Synthesis and Fracture Characteristics of TiB2-TiAl Composites with a Unique Microlaminated Architecture

Fabrication, Microstructure Characterization and Fracture Behavior of a Unique Micro-Laminated TiB-TiAl Composites

Macro-microscopic Morphology and Phase Analysis of TiAl-based Alloys Sheet Fabricated by EB-PVD Method

Preparation and Characterization of Novel Ti(Al)–TiB2/Ti3Al Metallic-Intermetallic Laminated Composites

Phase composition and microanalysis of TiAl-based alloys sheet by electron beam-physical vapor deposition

Optimum design, microstructure and mechanical properties of Ti/Ti 3Al multi-layered materials

Microstructure and Mechanical Properties of Ti-Al-Ti-Ti2AlNb Laminated Composites Based on the Ductile-brittle Structure

Processing and mechanical behavior of laminated titanium–titanium tri-aluminide (Ti–Al3Ti) composites

Optimum Design, Microstructure and Mechanical Properties of Ti/Ti3al Multi-Layered Materials

Synthesis and Mechanical Properties of Innovative (Tib/ti)-Ti3al Micro-Laminated Composites

Laminated Ti-Al Composites: Processing, Structure and Strength

Fabrication Of Tial Matrix Composite Sheetes With Controlled Micro-Laminated Architecture By A Solid-Liquid Reaction