Abstract:Selective laser melting (SLM) is a powerful additive manufacturing (AM) technology, of which the most prominent advantage is the ability to produce components with a complex geometry. The service performances of the SLM-processed components depend on the microstructure and surface quality. In this work, the microstructures, mechanical properties, and fracture behaviors of SLM-processed Ti-6Al-4V alloy under machined and as-built surfaces after annealing treatments and hot isostatic pressing (HIP) were investigated. The microstructures were analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscopy (TEM). The mechanical properties were measured by tensile testing at room temperature. The results indicate that the as-deposited microstructures are characterized by columnar grains and fine brittle martensite and the asdeposited properties present high strength, low ductility and obvious anisotropy. After annealing at 800–900°C for 2–4 h and HIP at 920°C/100MPa for 2 h, the brittle martensite could be transformed into ductile lamellar (α+β) microstructure and the static tensile properties of SLM-processed Ti-6Al-4V alloys in the machined condition could be comparable to that of wrought materials. Even after HIP treatment, the as-built surfaces could decrease the ductility and reduction of area of SLM-processed Ti-6Al-4V alloys to 9.2% and 20%, respectively. The crack initiation could occur at the columnar grain boundaries or at the as-built surfaces. The lamellar (α+β) microstructures and columnar grains could hinder or distort the crack propagation path during tensile tests.

Influence of Process Parameters of Forming Characteristics on Ti-6Al-4V Fabricated by Selective Laser Melting

The effect of process parameters on the physical and mechanical properties of Ti fabricated by selective laser melting using ball milled powders

Process parameter optimization for selective laser melting Ti-6Al-4V with high layer thickness

Effect of Processing Parameters on Tensile Properties and Microstructure of Selective Laser Melted AlSi10Mg Alloy

Role of processing parameters on relative density, microstructure and mechanical properties of selective laser melted titanium alloy

Investigation on influence of selective laser melting parameters on mechanical properties of Ti-6Al-4V alloy

Effect of Process Parameters and Layer Thickness on the Quality and Performance of Ti-6Al-4V Fabricated by Selective Laser Melting

Influence of Typical Technological Parameters on the Forming Quality of TA1 in Selective Laser Melting

Microstructure and inclusion of Ti–6Al–4V fabricated by selective laser melting

Processing Parameter Effects on Residual Stress and Mechanical Properties of Selective Laser Melted Ti6Al4V

Characteristics of Metal Specimens Formed by Selective Laser Melting: A State-of-the-Art Review

Tensile Behavior of Ti-6Al-4V Alloy Fabricated by Selective Laser Melting: Effects of Microstructures and As-Built Surface Quality

Study on the fabricating process of LaB6 reinforced Ti6Al4V by selective laser melting

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Application of Selective Laser Melting Technology Based on Titanium Alloy in Aerospace Products

Study on the effects of the processing parameters on the single tracks and the block support structures fabricated by selective laser melting

Effect of Overlapping Remelting on Microstructures and Mechanical Properties of Selective Laser‐Melted Ti‐6Al‐4V Alloy

Effects of HIP Process Parameters on Microstructure and Mechanical Properties of Ti-6Al-4V Fabricated by SLM

Study of the Effect of Selective Laser Melting Process Parameters on Overhang Structures

Densification, Tailored Microstructure, and Mechanical Properties of Selective Laser Melted Ti–6Al–4V Alloy via Annealing Heat Treatment

Coupling Analysis on Microstructure and Residual Stress in Selective Laser Melting (SLM) with Varying Key Process Parameters