Preparation and application of chlorinated polyethylene rubber/methacrylic acid (CSM/PMAA) membranes for diffusion dialysis

Farui CHONG,Jingwen WANG,Ruitao JIN,Manli WANG,Jibin MIAO,Weibin ZHOU,Jiasheng QIAN
DOI: https://doi.org/10.16159/j.cnki.issn1007-8924.2017.05.008
2017-01-01
Abstract:A series of composite cationic ion exchange membranes for alkali recovery have been prepared by using chlorinated polyethylene rubber (CSM) and methacrylic acid (MAA) as framework and functional monomer,respectively.An interpenetrating network (IPN) structure was formed by free radical polymerization and subsequent crosslinking induced by the introduction of dipentamethylene thiuram hexasulfide (DPTT).The asprepared membranes possessed water uptake (WR) of 5.38%~28.3% and ion exchange capacity (IEC) of 3.57 ~5.12 mmol/g with good thermal stability (initial degradation temperatures were in the range of 260~281 ℃C) and mechanical stability (tensile strength and elongation at break were in the range of 19.3~33.4 MPa and 140.7%~524.9%,respectively).The membranes exhibited excellent alkali resistance,with a weight loss of 0.85%~2.08% after immersing in 65 ℃ 2 mol/L NaOH solution for 60 h,which can be attributed to the high alkali resistance of CSM and the IPN structure.The membranes were successfully used for alkali recovery from NaOH/Na2WO4 mixtures via a diffusion dialysis process and the membrane performance was optimal when the dosage of DPTT was 5% at 55 ℃.Under these conditions,the dialysis coefficient of OH (UoH) was 0.003 4 m/h,while the separation factor (S) was 16.8.
What problem does this paper attempt to address?