Abstract:Polymers are widely used in bearing applications. In the case of water-lubricated stern tube bearings, thermoplastic polyurethane (TPU)-based composites are used due to their excellent wear resistance, corrosion resistance, and tunable mechanical properties. Their tribological performance, however, depends on operating conditions. In this work, TPU was blended with carbon fiber, graphene platelet, and ultra-high molecular weight polyethylene (UHMWPE). Friction tests of TPU based-composites against copper countersurface were carried out in water to mimic the actual operating conditions of the bearing. Most of the resulting contacts were in the boundary lubrication regime, in which friction was attributed to both contact mechanics of asperities as well as water lubrication. Our results show that the viscoelasticity of TPU has a considerable impact on its tribological performance. Water lubrication at 50 °C promotes the softening of polymer surface material during sliding, resulting in higher fluctuation in the coefficient of friction and wear loss. This is attributed to the reduced thermomechanical properties. In addition, Schallamach waviness is observed on worn surface. The tribological properties of TPU are significantly improved by the inclusion of carbon fiber, graphene platelet, and UHMWPE. The formation of graphene transfer-layers and UHMWPE transfer film reduces friction and wear loss, while the inclusion of carbon fiber enhances wear resistance due to improved mechanical properties and load bearing capacity.

Experimental Study on Friction Characteristics of Water-lubricated Composite-material Bearings

Researches on Friction Performance of Water-Lubricated Polymer Composite Journal Bearings Based on Experiments

Tribological behavior of modified polyetheretherketone composites in sliding against stainless steel under water lubrication

A Comparative Investigation of the Tribological Behavior and Wear Mechanism of Bronze-graphite Composite under Dry- and Water-lubricated Sliding Against Steel

Friction and Wear of Self-Mated SiC and Si 3 N 4 in Green Water-Based Lubricant

Experimental Study on Material Properties of Bearing Bush of Water Lubricated Bearing

Experimental investigation on dry frictional behavior of the two self-lubricating composites under heavy loading conditions

Tribological and physical properties of PTFE-NBR self-lubricating composites under water lubrication

Tribological and Vibration Properties of Three Different Polymer Materials for Water-Lubricated Bearings

Tribological evaluation of thermoplastic polyurethane-based bearing materials under water lubrication: Effect of load, sliding speed, and temperature

Tribological Performance Study of Low-Friction PEEK Composites under Different Lubrication Conditions

Tribological behavior of PTFE/Nomex/phenolic composite lubricant under cold forming condition in the bearing assembly process

A study on improving friction and wear performance of bearing bush in radial piston hydraulic motor

Experimental Investigation of Tribological Performance of Ptfe-Derived Solid Lubricants in Sliding Building Bearings

Ultralow friction of PEEK composites under seawater lubrication

Tribological Properties Of Polytetrafluoroethylene-Based Composite In Different Lubricant Media

Experimental investigation on frictional behavior and sealing performance of different composites for seal application

A state-of-art review on the water-lubricated bearing

Comparative Investigation on the Friction and Wear Behaviors of Carbon Fabric–Reinforced Phenolic Composites under Seawater Lubrication

Study on ultra-low friction performance of PTFE film combined with water-based ionic liquid lubrication at electrical contact interfaces

Carbon Fibre Reinforced Bisphenol-a Type SPEEK Composite for Water Lubricated Superlubricity