Preparation of carbon fiber reinforced silicon carbide porous ceramiccomposites with three dimensional network structure

Lujun XIAO,Xiaozhong HUANG,Zuojuan DU,Xiuzhi TANG

DOI: https://doi.org/10.3969/j.issn.1001-9731.2018.01.002

2018-01-01

Abstract:By combination of precursor infiltration pyrolysis (PIP)and three-dimentional printing methods,carbonfiber reinforced silicon carbide porous ceramic composites (3D-Cf/SiC porous ceramic composites)withthree-dimensional open-celled network structure were successfully fabricated.Carbide fibers and polycarbosilaneused as raw materials were sintered at 1250 ℃ in argon atmosphere.The phase composition,microstructureand compressive strength were characterized by X-ray diffraction (XRD),scanning electron microscopy (SEM)and universal material testing machine.The results show that the phase composition of 3D-Cf/SiC porous ceramiccomposites consisted ofβ-SiC and C.As the diameter of porous ceramic composites increased,the porositydecreased and the bulk density,skeleton density,compressive strength and thermal conductivity increased.When the diameter of the porous ceramic composites increased from 1.0 to 2.5 mm,the pore size increased from1.0 to 2.5 mm,the porosity increased from 63％ to 82％,and the bulk density,skeleton density,compressivestrength and thermal conductivity decreased from 0.85 to 0.45 g/cm3 ,1.52 to 0.92 g/cm3 ,8.00 to 4.20 MPa and2.00 to 1.20 W/(m·K),respectively .