Addition of Co, Fe to regulate the structure and hydrogen storage property of (TiZr)1.1Cr2.0 alloy

Li XU,Peng SHENG,Jigang LI,Xiaojing JIANG,Xingguo LI,Haizhen LIU,Shuangyu LIU,Guangyao ZHAO,Bo WANG,Yu HAN,Xin CHEN

DOI: https://doi.org/10.3969/j.issn.1001-9731.2017.10.002

2017-01-01

Abstract:(Ti0.9Zr0.1)lnCr2.0-xMx(M=Co or Fe,x=0-0.1) alloys were prepared by argon plasma arc melting,and X-ray diffraction (XRD),pressure-composition-temperature (PCT),differential scanning calorimetry (DSC) were performed on the structure and hydrogen storage capacity of this series of alloys.The result showed that the structure of this kind alloys was all C14 type Laves phase.From the PCT measurement,the hydrogen absorption and desorption of this alloys had weak hysteresis effect.Using some amount of Co or Fe to substitute for partial Cr of (Ti0.9 Zr0.1)1.1 Cr2.0 decreased the volume of cell unit,and increased the absorption platform pressure.At the condition of 293-304 K,the addition of Co had no obvious effect on the maximum hydrogen storage,but reduced the reversible hydrogen storage.The maximum hydrogen storage didn't change at 293-304 K and the reversible hydrogen storage increased at 293-324 K when Fe substituted for partial Cr.The temperature of desorption about the residual hydrogen was not impacted by Co substituting for partial Cr,but increased from 613-713 K to 653-733 K when Fe replaced partial Cr.