Preparation and its H2-permeable characteristics of Nd doped La5.5 WO12-δ

Lei JIA,Ling WANG,Lei DAI,Yue-hua LI,Hui-zhu ZHOU

DOI: https://doi.org/10.3969/j.issn.1001-9731.2014.z2.032

2014-01-01

Abstract:Mixed proton-electron conductors of (La1-xNdx)5.5 WO12-δ(x=1/3,1/2)were successfully synthe-sized by the solid state reaction route.The phase composition and microstructures of the samples were investiga-ted by XRD and SEM,respectively.Chemical stability against humid CO2 was tested.The total conductivities of the samples in air and wet 5% H2/Ar atmospheres were measured by the AC impedance spectroscopy.Hydro-gen permeation performance of the membranes was tested at different temperatures and hydrogen partial pres-sures.The results indicate that the samples sintered at 1 550 ℃ were cubic fluorite structure and the samples were extremely dense.The samples are quite stable in humid CO2 atmosphere.The samples have higher conduc-tivities in wet 5% H2/Ar and (La1/2 Nd1/2 )5.5 WO12-δpresents a high conductivity in wet 5% H2/Ar,which was about 6.58×10-3 S/cm at 850 ℃.Using 50% H2/N2 as feed gas,the highest hydrogen flux for (La1/2 Nd1/2 )5.5 WO12-δmembrane with thickness of 1.56 mm was 0.079 mL/(min??cm2)at 900 ℃.