Abstract:A novel nanostructured material composed of WS2/WO2.9/C membranes with free-standing and flexible feature, which were synthesized via a two-step heat treatment of ammonium tetrathiotungstate ((NH4)2WS4) and polyacrylonitrile (PAN) spin-coated onto graphite foils. These two precursors decompose at high temperature (850°C) forming WS2 and C species, while the introduction of trace amount of oxygen leads to the formation of WO2.9 nanowires. First, (NH4) 2WS4 and PAN were dissolved in N,N-dimethylformamide (DMF). The mixture was stirred until a homogeneous solution was formed. The precursor solution was then spin-coated onto a substrate. After drying under ambient conditions, the coated substrate was loaded into a chemical vapor deposition (CVD) system for thermal treatment in the presence of sulfur. The precursor on the substrate was first annealed at 500°C in Ar/H2 flow to decompose (NH4) 2WS4, and then heated up to 850°C and annealed under an Ar flow and vaporized sulfur, finally the system was allowed to cool down to room temperature. Trace amounts of oxygen were induced into the CVD system during the cooling process, thus leading to the formation of tungsten oxide at 700°C. As-synthesized WS2/WO2.9/C samples on graphite foils exhibit excellent mechanical flexibility. Scanning transmission electron microscopy (STEM) coupled with high-angle annular dark-field (HAADF) imaging, reveals the fine structure of the WS2/WO2.9/C sample. STEM-EDS mappings indicate that the distributions of S and O are correlated with W, while the density of C is rather low in W-rich regions, thus implying that tungsten sulfide and oxide are the main phases. In addition to elemental distribution, electron microscopy also reveals the crystalline structure of the WS2/WO2.9/C hybrid. High-resolution TEM (HRTEM) image demonstrates widely separated fringes with the closest spacing of 0.62 nm, which is in agreement with the d-spacing of of 2H-WS2.

A CO2‐stable Hollow‐fiber Membrane with High Hydrogen Permeation Flux

CO2-tolerant U-shaped Hollow Fiber Membranes for Hydrogen Separation

Niobium and Molybdenum Co-Doped La5.5WO11.25−δ Membrane with Improved Hydrogen Permeability

CO2-tolerant Ni-La5.5WO11.25-δ Dual-Phase Membranes with Enhanced H2 Permeability

Enhanced H2 production by using La5.5WO11.25-δ-La0.8Sr0.2FeO3-δ mixed oxygen ion-proton-electron triple-conducting membrane

Stiff Metal–organic Framework–polyacrylonitrile Hollow Fiber Composite Membranes with High Gas Permeability

Enhanced Hydrogen Permeability of Mixed Protonic-Electronic Conducting Membranes through an In-situ Exsolution Strategy

Phase-inversion Synthesize of Asymmetric-Structured La5.5W0.6Mo0.4O11.25-δ Membranes with Enhanced Hydrogen Permeation Flux

Effect of the La/W Ratio in Lanthanum Tungstate on the Structure, Stability and Hydrogen Permeation Properties

Hydrogen Permeability Through Nd5.5W0.35Mo0.5Nb0.15O11.25-δ Mixed Protonic-Electronic Conducting Membrane

Hollow Fiber Contained Hydrogel-Ca Membrane Contactor for Carbon Dioxide Removal from the Enclosed Spaces

Metal-Organic Framework/Pvdf Composite Membranes with High H-2 Permselectivity Synthesized by Ammoniation

Asymmetric Membrane Structure: an Efficient Approach to Enhance Hydrogen Separation Performance

A mixed electronic and protonic conducting hydrogen separation membrane with asymmetric structure

Effect of Pt Layer on the Hydrogen Permeation Property of La5.5W0.45Nb0.15Mo0.4O11.25-δ Membrane

Tailoring Hydrogen Separation Performance Through the Ceramic Lanthanum Tungstate Membranes by Chlorine Doping

Subnanometer Nanowire‐Reinforced Construction of COF‐Based Membranes with Engineering Biomimetic Texture for Efficient and Stable Proton Conduction

Co2-Resistant Hydrogen Permeation Membranes Based on Doped Ceria and Nickel

Bioinspired Heterogeneous Construction of Lignocellulose‐Reinforced COF Membranes for Efficient Proton Conduction

Noble-Metal-Free Hybrid Membranes for Highly Efficient Hydrogen Evolution

Vacuum‐Assisted Confined Growth of MOF@COF Composite Membranes with Enhanced Hydrogen Permselectivity