Effect of Er2O3 addition and calcining temperature on CaTiO3 material prepared by solid reaction
Di An,Xudong Luo,Pengcheng Liu,Zhipeng Xie,Ting Li
DOI: https://doi.org/10.3969/j.issn.1001-1935.2018.01.001
2018-01-01
Refractories
Abstract:CaTiO3materials were prepared using analytically pure CaO and TiO2as starting materials,and Er2O3as an additive to improve the sintering characteristics.After ball milling the stoichiometric CaO and TiO2,and extra-added Er2O3(1%,2%,3%,and 4%,by mass),the mixtures were synthesized into CaTiO3 materials by the solid reaction sintering method.The phase composition,microstructure and element com-position of the products were investigated by XRD,SEM and EDS.The cell parameters were determined by X'Pert High Score Plus software to analyze the relationship between ionic substitution and cell volume.The results indicate that when adding a little Er2O3,the displacement reaction between Er3+and Ti4+happens preferentially,the CaTiO3cell structure distorts,thus the cell volume increases.When the addition of Er2O3 increases,the displacement reaction between Er3+and Ca2+happens,the CaTiO3cell shrinks,thus the cell volume decreases.The lattice distortion caused by the solid solution of Er2O3and CaTiO3accelerates the ion diffusion and promotes the sintering of CaTiO3material,and the occurred structure defects accelerate the growth of CaTiO3grains.With the calcining temperature rising,thermal defects increase,and the sinte-ring property of synthesized CaTiO3is promoted.