Sodium Modification Study on a Ca-based Bentonite from Tiandong,Guangxi

Wang Guifang,Pan Yiren,Ma Shaojian,Li Hengjun,Xiao Huizhen,Yang Jinlin

2017-01-01

Abstract:Because most of bentonites are calcium-based bentonites in China,and the content of montmorillonite is rela-tively low,it is difficult to use raw bentonite in the development of bentonite slurry with high viscosity and low filtration loss. Based on the purification of acalcium-based raw bentonite in Tiandong,Guangxi,modification of calcium-based bentonite by so-dium carbonate was studied. Effects of slurry concentration,sodium carbonate dosage,modification temperature and time on the properties of Na-bentonite were investigated. The results showed that the 600 r/min and 300 r/min viscosity of Na-bentonite in-creased firstly and then decreased with the increase of the slurry concentration,dosage of sodium carbonate and modification time. While the filtration loss increased with the increase of the slurry concentration,and it appeared to be the trend of firstly decrease and then increase with increasing modification time. With increase of slurry concentration,the dynamic plastic ratio increased firstly and then decreased. Viscosity of Na-bentonite was not increased by increasing the modification temperature, while filtration loss would be increased. Under the conditions of slurry concentration of 5%,sodium carbonate amount of 4%, modification temperature of 25 ℃ and modification time of 20 min,600 r/min viscosity of the prepared bentonite reached 26 mPa·s,dynamic plastic ratio was 0. 181 Pa/( mPa·s) ,and filtration loss was 17. 6 mL.