Preparation of modified halloysite nanotubes/Pebax1657 hybrid membranes and gas separation performance thereof

Qing Zhao,Shaojian He,Jun Lin,Qianguo Lin,Xiaoya Duan

DOI: https://doi.org/10.3969/j.issn.1000-8144.2019.11.005

2019-01-01

Abstract:The halloysite nanotubes(HNTs) were modified by surface coating method using polydopamine and polyethyleneimine as raw materials to obtain inorganic filler PDH. The organic-inorganic hybrid membrane was prepared by using polyether copolyamide Pebax1657 as polymer substrate and PDH as inorganic filler. The structure of the membrane was characterized by SEM, XRD,DSC,etc. The mechanical properties and gas separation properties of the membranes were tested. The experimental results show that PDH was uniformly dispersed in Pebax1657,and the compatibility between the two was good. The hydrogen bond formed between PDH and Pebax1657 hinders the molecular chain movement and leads to the increase of glass transition temperature and the decrease of crystallinity. With the increase of PDH content,the density of hybrid membrane increased gradually,the tensile strength increased first and then decreased,the elongation at break decreases, the permeability coefficients of CO2 and N2 of hybrid membranes increased. Compared with pure Pebax1657 membrane,the permeability coefficients and selectivity of hybrid membranes gradually approached Robeson upper bound,and the gas separation performance was improved.