Abstract:Longitudinal crack defects are a frequent occurrence on the surface of thin slabs during the high-speed continuous casting process. Therefore, this study undertakes a detailed analysis of the solidification characteristics of hyper-peritectic steel thin slabs. By establishing a three-dimensional heat transfer numerical model of the thin slab, the formation mechanism of longitudinal cracks caused by uneven growth of the initial shell is determined. Based on the mechanism of longitudinal crack formation, by adjusting the performance parameters of the mold flux, the contradiction between the heat transfer control and lubrication improvement of the mold flux is fully coordinated, further reducing the incidence of longitudinal cracks on the surface of the casting thin slab. The results show that, using the optimized mold flux, the basicity increases from 1.60 to 1.68, the F- mass fraction increases from 10.67% to 11.22%, the Na2O mass fraction increases from 4.35% to 5.28%, the Li2O mass fraction increases from 0.68% to 0.75%, and the carbon mass fraction reduces from 10.86% to 10.47%. The crystallization performance and rheological properties of the mold flux significantly improve, reducing the heat transfer performance while ensuring the lubrication ability of the molten slag. After optimizing the mold flux, a surface detection system was used to statistically analyze the longitudinal cracks on the surface of the casting thin slab. The proportion of longitudinal cracks (crack length/steel coil length, where each coil produced is about 32 m long) on the surface of the thin slab decreases from 0.056% to 0.031%, and the surface quality of the thin slab significantly improves.

Analysis and Control of Factors of Triangular Area Cracking of Continuously Cast Slab at Nanjing Steel

Simulation Analysis of Thermal Stress During Casting Process of Large-Sized Alloy Steel Ingot

A Method to Control the Transverse Corner Cracks on a Continuous Casting Slab by Combining Microstructure Analysis with Numerical Simulation of the Slab Temperature Field

Steel Edge Cracking Analysis and Improvement Measures

Analysis and control of surface cracks in a B-bearing continuous casting blooms

Analysis of Internal Cracks in Continuous Casting Slabs with Soft Reduction

The Causes and Control of Longitudinal Edge Cracks of the Plate

Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel

Analysis of Longitudinal Cracking and Mold Flux Optimization in High-Speed Continuous Casting of Hyper-Peritectic Steel Thin Slabs

Improvement on slab surface quality of Nb microalloyed steels at No.2 steelmaking plant WISCO

Prevention of transverse corner crack in continuous casting slab by adjusting cooling schedule

Investigation on Longitudinal Surface Cracks of CC Slabs for Container

Continuous Casting Mould for Square Steel Billet Optimised by Solidification Shrinkage Simulation

Some Aspects of Continuous Casting of Low Carbon Microalloyed Steels with Niobium and Titanium

Analysis and Control of Central Cracks in the Bloom Continuous Casting of Microalloy 49mnvs3 Steel

Characterization and Control of Secondary Phase Precipitation of Nb-V-Ti Microalloyed Steel during Continuous Casting Process

Analysis of Internal Cracks in High Carbon Casting Bloom Induced by Soft Reduction Process and Its Improvement Using Numerical Simulations and Industrial Experiments

Analysis and Control of the Slab Hot Ductility Behaviors Based on Nozzle Arrangement during Continuous Casting

Numerical Simulation of Central Shrinkage Crack Formation in a 234-T Steel Ingot

Prediction and Analysis on Formation of Internal Cracks in Continuously Cast Slabs by Mathematical Models.

Improving the casting process of peritectic steel grades