Abstract:To scientific understanding the effect of a slight change in carbon content near the upper/lower limit on alloys, five sets of WC-10Co cemented carbides were prepared with the carbon content of 5.34 wt%, 5.36 wt%, 5.44 wt %, 5.53 wt% and 5.56 wt% respectively. The properties of the alloys are analyzed by SEM, XRD, Hardness tester, universal testing machines, HSR-2 M tribometer, and surface characterisation. The results showed that the existent of multi-steps proved that the WC coarsening process was governed by 2-D nucleation in the alloy with low carbon content. On the contrary, the low W solubility in Co and the low melting point of Co binder accelerated the dissolution-precipitation process with increasing carbon content. At this time, the morphologies of WC grains tented to be the triangular shape without multi-steps due to the continuous grain growth. Additionally, the increasing of the value of carbon content brought about the coarser WC grain size, and the particle size distribution with ?double peak? was also observed in the alloy with free carbon. Further analysis of XRD, the various dissolution of W in Co binder phase brought about a minor different intensity of the basal plane (0001) peaks. Moreover, a slight change in carbon content near the upper/lower limit also significantly affected the mechanical properties of alloys. The cemented carbides with 5.44 wt% carbon content in two phase range exhibited a combination of superior mechanical properties and wear resistance.

Effect of coarse grained WC addition on microstructure and mechanical properties of WC-Co cemented carbide

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

The effects of micron WC contents on the microstructure and mechanical properties of ultrafine WC-(micron WC-Co) cemented carbides

The Enhancement of the Microstructure and Mechanical Performances of Ultrafine WC-Co Cemented Carbides by Optimizing Cr2(C,N) Addition and WC Particle Sizes

Effect of Vc and Nbc Additions on Microstructure and Properties of Ultrafine Wc-10co Cemented Carbides

Effect of (cr, V)2(C, N) on the Microstructure and Mechanical Properties of WC-10Co Cemented Carbides

Microstructure and mechanical properties of WC–Co-based cemented carbide with bimodal WC grain size distribution

Effect of Carbon Content on Microstructure and Mechanical Properties of WC-10Co Cemented Carbides with Plate-Like WC Grain

Comparative Study on Microstructure and Mechanical Properties of Coarse-grained WC-based Cemented Carbides Sintered with Ultrafine WC or (W+C) as Additives

Effects of Cr2(C,N) Addition on Microstructure and Comprehensive Mechanical Properties of Ultrafine Cemented Carbide

Effect of Cobalt Content on the Microstructure and Mechanical Properties of Coarse Grained WC-Co Cemented Carbides Fabricated from Chemically Coated Composite Powder

Effect of WO3 Content on Microstructure and Properties of Ultracoarse Grained Cemented Carbide

Microstructures and Mechanical Properties of WC-Co-xCr-Mo Cement Carbides

Effect of particle size and high-energy ball milling time on microstructure and mechanical properties of WC-10Co cemented carbides with plate-like WC grains

Effect of Cr3C2 Addition on Microstructure and Mechanical Properties of WC-CoNiFe Cemented Carbides

Effects of Submicron WC Addition on Structures, Kinetics and Mechanical Properties of Functionally Graded Cemented Carbides with Coarse Grains

The effects of fine WC contents and temperature on the microstructure and mechanical properties of inhomogeneous WC-(fine WC-Co) cemented carbides

Influence of Micron WC Addition on the Microstructure and Mechanical Properties of Ultrafine WC–Co Cemented Carbides at the Elevated Temperature

The influence of different content of Cr on microstructure and properties of WC-Co cemented carbide

Influence of VC/Cr3C2 and Mixed Carbon Content on Microstructure and Properties of Ultrafine WC-0.5Co Cemented Carbide

Effect of a Slight Change in Carbon Content Near the Upper/lower Limit on the Microstructure and Mechanical Properties of WC-10Co Cemented Carbides