Analysis of residual stress in green compact of circular thin-wall powder metallurgy parts

Rui Zhou,Dong Xie,Lulu Li,Jianguo Zhang

DOI: https://doi.org/10.14186/j.cnki.1671-6620.2017.03.012

2017-01-01

Abstract:Esidual stress of the compacted circular thin - walled powder metallurgy parts was analyzed, and the modified Drucker-Prager Cap model was used to simulate the pressing, unloading, and stripping process of the metal powder compact. Influences of the geometrical parameters ( aspect ratio and ratio of thickness to diameter) of the green compact and pressing conditions (friction conditions and die taper) on the residual stress in the green compact were investigated. The results showed that the residual stress after crust stripping has a significant compressive stress layer on the side of the green compact. The inside of the green compact there is a tensile stress region, and the value is smallest in the center of the compact. With increase of the ratios of height to diameter and thickness to diameter, the residual stress decreases; With increase of the friction coefficient, the axial residual compressive stress of the green compact surface increases and the tensile stress inside the green compact also increased;An appropriate increase in the die taper is beneficial to release the stress in the green compact and reduce the residual stress. Through the orthogonal simulation test and the analysis of variance, it was found that the ratio of thickness to diameter and the die taper have a more significant effect on the residual stress of the green compact after forming and stripping the metal powder.