Effect of Rare Earth Content on Corrosion Resistance of Extruded Cu-7Ni-7Al-2Fe-2Mn Alloy

Li Xiaomeng,Zhang Yanmin,Guo Xiuhua,Song Kexing,Li Zhou,Mi Xujun

DOI: https://doi.org/10.11785/S1000-4343.20170505

2017-01-01

Abstract:This paper studied the influence of RE content on microstructure and corrosion resistance of extruded Cu-7Ni-7Al-2Fe-2Mn alloy.The results showed that the alloy was mainly uniform corrosion,when the soaking time was less than 48 h (12,24 and 48 h),the rare earth content of the alloy corrosion sensitivity was higher.The corrosion rates were 0.1720,0.1311 and 0.1065 g·m-2·h-1 when the rare earth contents were 0.0000％,0.0146％ and 0.0352％ respectively after soaked 24 h,with increase of the rare earth content and decrease of the sensitivity.The alloy corrosion rate differences were 0.1311 and 0.0328 g·m-2·h-1,that rare earth contents were 0.0000％,0.0146％ and 0.0352％ respectively after soaked 24 h,it was reduced by 42％ and 15％;the rare earth element content of the alloy had no significant improvement to all of the corrosion rates,alloy corrosion surface passivation film increased with the addition of rare earth elements.For the rare earth content the higher of the quality of the passivation film before 48 h,the smaller the impact of rare earth passivation film after 48 h.With the addition of rare earth,the electrochemical properties of the alloy was improved,the charge transfer resistance Rt maximum reached 1.651 x 104 Ω·cm2 when the rare earth content 0.0352％,the protection performance of the passivation film was best.