Microstructure and Electrochemical Characteristics of Melt-Spinning Alloy Ml( NiCoMnAl)5

文明芬,陈廉,佟敏,陈德敏,翟玉春

DOI: https://doi.org/10.3321/j.issn:1000-4343.2001.01.012

2001-01-01

Abstract:The microstructure and electrochemical characteristics of Ml(NiCoMnAl)5 alloys prepared by both the melt-spinning method and the conventional induction melti ng were investigated and compared. SEM and XRD studies show that the microstruct ure of melt-spinning alloys is columnar structure. With increasing melt-spinni ng rate, the crystal grains become finer and preferentially grow into (111)［111 ］ direction. The melt-spinning and cast alloys belong to CaCu5 type hexagona l crystal structure. The electrochemical measurements show that the initial capa cities of melt-spinning alloy electrodes are all above 210 mAh*g－1 and have good activation behavior, reaching their maximum capacities after two charg e-discharge cycles. The maximum capacity (294 mAh*g－1) of melt-spin ning (10 m*s－1) alloy electrodes is as same as that of as-cast alloy e lectrode, and the stability of charge-discharge cycles of all melt-spinning al loy electrodes is better than that of the as-cast alloy electrodes. When charge d at 600 mA*g－1, the capacity of melt-spinning (10 m*s－1) alloy electrode reach 65% of its maximum capacity after about 45 min, and has better high rate discharge capability; but with the cycle number increasing, the stabil ity of its capacity is less than that electrodes of melt spinning rate of 40 m *s-1.