Interfacial structure of MgO and MgAl2O4with pure Al and their nucleation behavior

ZHANG Di,WANG Lu,XIA Ming-xu,LI Jian-guo
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2017.08.01
2017-01-01
The Chinese Journal of Nonferrous Metals
Abstract:The nucleation behavior of common oxides MgO and MgAl2O4in AlMg alloys were investigated by scanning electron microscopy, transmission electron microscopy and X-ray diffraction. The results show that, at high temperatures, Al melt would react with MgO and MgAl2O4substrates to formed Al2O3at contacting interface. Among them, the reaction of Al/MgO is a multi-step reaction and MgAl2O4 is an intermediate reaction product. The interfacial reactionlayer Al2O3 hinders liquid Al from contacting MgO or MgAl2O4substrates, inhibiting their interfacial reaction to some extent. The interfacial reaction corrodes the exposed planes of original substrates, leading to scattered growth orientations of the new grains. TEM results of three detected nucleation interfaces Al/Al2O3, Al/MgO and Al/MgAl2O4 indicate that either new formed Al2O3or original MgO and MgAl2O4could all act as effective heterogeneous substrates to trigger nucleation process of Al, but with different nucleation potencies.
What problem does this paper attempt to address?