Abstract:The effect of sintering atmosphere (air and Ar) and temperature (1100, 1200, 1300 °C) on the microstructure, mechanical properties, and bioactivity of hydroxyapatite/tantalum (HA/Ta) composites were systematically investigated by pressureless sintering of the mixture of HA and Ta powders. It shows that the sintering atmosphere greatly impacts the phase composition and microstructure of the HA/Ta composites. The higher diffusion of atoms promotes shrinkage and causes deeper reaction fusion between the HA matrix and Ta, which improved the interfacial binding of the HA/Ta composites. The refined grain structure and improved interfacial binding obtained within the Ar atmosphere compared to the air atmosphere benefit the mechanical properties. The maximum bending strength and shrinkage observed for the composites sintered at 1300 °C in the Ar atmosphere are 27.24 MPa and 6.65%, respectively. The cell counting kit-8 (CCK-8) method was used to investigate the in vitro cytocompatibility of HA/Ta composites. The results revealed that the HA/Ta composites sintered with different conditions have no cytotoxicity. The simulated body fluid (SBF) soaking results showed that all of the studied composites possess desirable bioactivity, as demonstrated by their ability to form calcium-deficient carbonate apatite layer on the surfaces. For composites sintered at 1300 °C, the surface apatite layer coverage of the composites obtained in the Ar atmosphere was increased by 139.7% than the ones obtained in air, which confirmed an enhanced bioactive mineralization ability. The results indicated that the HA/Ta composites sintered at 1300 °C in Ar possess desirable mechanical properties and bioactivity. This work opens up the new possibility for preparing HA-based composites and is of great value in biomedical applications.This article has not yet been cited by other publications.

Study on microstructure and biological activity in vitro of Ti/HA bio-composite

Significantly Accelerated Osteoblast Cell Growth on TiO 2 /SrHA Composite Mediated by Phenolic Compounds (BHM) from Hippocamp us kuda Bleeler.

In vivo bioactivity of Ti/HA biocomposites fabricated by powder metallurgy methods

Porous Ti/HA biocomposites for biomaterial applications

Correlations Between the in Vitro and in Vivo Bioactivity of the Ti/HA Composites Fabricated by a Powder Metallurgy Method.

Microstructure and in Vitro Bioactivity of 50ti/ha Biocomposite

Function-structure-integrated Ti-HA coatings on TiNbZr with enhanced mechanical properties and bioactivity prepared by spark plasma sintering

Microstructure and in Vitro Bioactivities of HA/Ti Composites Prepared by Hot Isostatic Pressing

Tribological behavior and in vitro biocompatibility of powder metallurgical Ti–15Mo/HA composite for bone repair

Microstructure and Properties of Ti35Nb2.5Sn5HA Biocomposites by Powder Metallurgy and Sintering

HA/Ti composite for biomedical application by mechanical milling

Surface and interface analysis of HAP/TiO2 composite films on Ti6Al4V

Effects of Sn Content on the Microstructure, Mechanical Properties and Biocompatibility of Ti–Nb–Sn/hydroxyapatite Biocomposites Synthesized by Powder Metallurgy

Microwave sintering of porous Ti–Nb-HA composite with high strength and enhanced bioactivity for implant applications

Surface and interface analysis of HAP/TiO2 composite films on Ti6A14V

Preparation of Hierarchical Porous Structure on Ti Surface and Bioactivity

Preparation and bioactive surface modification of the microwave sintered porous Ti-15Mo alloys for biomedical application

Ti-Nb-Sn-Hydroxyapatite Composites Synthesized by Mechanical Alloying and High Frequency Induction Heated Sintering

Characterisation and Mechanical Adhesion of HAP/TiO2 Composite Films on Ti6Al4V Processed by Sol-Gel Method

Fabrication of Hydroxyapatite/Tantalum Composites by Pressureless Sintering in Different Atmosphere

In vitro and in vivo performance of bioactive Ti6Al4V/TiC/HA implants fabricated by a rapid microwave sintering technique.