Effect of cryogenic treatment on QPQ layer on 42CrMoA steel surface

Xiaohui Zheng,Dongyu He,Xiaoting Liu,Jun Du,Jun Tan

DOI: https://doi.org/10.13251/j.issn.0254-6051.2017.08.033

2017-01-01

Abstract:Effect of -60 ℃ cryogenic treatment on QPQ layer of 42CrMoA steel surface was studied.The scanning electronic microscopy, X-ray diffraction, nano-indentation and scratch test were employed to evaluate the morphology, microstructure and mechanical properties of the QPQ layer, respectively.It is found that the QPQ treated layer on 42CrMoA steel surface consists of loose layer, nitride layer and diffusion zone;The loose layer is composed of oxide layer (<10 μm) and oxide-nitride blended zone (<5 μm);The hardness of nitrided layer (10-15 μm) is above 800 HV0.05 and the hardness in diffusion zone (0.3-0.4 mm) reduces gradually from 500 HV0.05 to 325 HV0.05(substrate hardness);The bonding strength between nitrided layer and diffusion zone is about 25 N.It is concluded that the cryogenic treatment at -60 ℃ does not considerably affect the hardness and bonding strength of nitrided and diffusion layers, but weakens the bonding between loose layer and nitrided layer which brings a large scale peeling off in the loose layer.