Thermodynamic calculation and analysis on equilibrium precipitate in Nb-Ti-IF steel

Tao Zou,Fuming Wang,Qingyong Meng

DOI: https://doi.org/10.13251/j.issn.0254-6051.2015.07.040

2015-01-01

Abstract:Equilibrium precipitates in Nb-Ti-IF steel in the temperature range from 0 to 1600 ℃ were calculated based on thermodynamic software Thermo-Calc.The effects of microalloying elements Nb and Ti on Nb precipitates and Ti precipitates were studied , respectively .In addition, the comparison of thermodynamic equilibrium calculation and microscopic observation for FeTiP precipitates was carried out .The results show that the main equilibrium precipitates in Nb-Ti-IF steel at temperatures from 0 to 1600 ℃ are FCC_A1#1, FCC_A1#2, LAVES_PHASE_C14, Ti4 C2 S2 , MnS and M3 P.When Ti content is more than 0.045%, the Ti content change almost has non effect on the FCC_A1#1 precipitates, but when Ti content is less than 0.045%, the Ti content change has effect on the FCC_A1#1 precipitates;when Ti content is more than 0.05%, the Ti content change almost has smaller effect on the Ti 4 C2 S2 precipitates; when Ti content is less than 0.05%, the Ti content change has marked effect on the Ti 4 C2 S2 precipitates.The optimum contents of micro-alloying elements Nb and Ti are 0.02%and 0.05%, respectively.