TEM characterization of the precipitation reaction in Ti–48Al–10Nb alloy

H.W. Liu,Y. Yuan,Z.G. Liu,J.-M. Liu,X.N. Zhao,Y.Y. Zhu
DOI: https://doi.org/10.1016/j.msea.2005.09.039
2005-01-01
Abstract:A detailed transmission electron microscopy (TEM) study has been made of the morphology and the crystallographic characteristics of precipitation of the γ1-Ti4Nb3Al9 in the γ-TiAl matrix in Ti–Al–Nb system. It is revealed that the γ1-Ti4Nb3Al9 precipitates, which are formed by a normal quench at 1473K and ageing treatment at 1073K, take needle-like morphology with a growing axis parallel to [001] direction of the matrix. The needle-like precipitates act as barrier grid to inhibit dislocation moving on the slipping plane {111} of the γ-TiAl matrix, which helps to improve the strength of the alloy. Selected electron microscopy analysis shows that the orientation relationship between the γ1 phase and the γ-TiAl matrix is [001]γ1//[001]γ, (100)γ1//(110)γ and (010)γ1//(1¯10)γ. The needle-like morphology of the precipitated phase is discussed with the coherency stress across the precipitate/matrix interface that is considered to be the main factor controlling the precipitate morphology.
What problem does this paper attempt to address?