Effects of Deforming Temperature on Grain-refining of 20Mn2 Steel Containing ZrC Particles

Xiao-tie DENG,Zhi-yi LIU,Qing-chun ZHENG

DOI: https://doi.org/10.3969/j.issn.0254-6051.2005.08.008

2005-01-01

Abstract:The grain-refining behaviors of 20Mn2 steel containing ZrC particles compressed with various degree of deformation (30%80%) at different temperature (8501150) were investigated by thermal simulating test.Microstructure analyses indicate that the role of ZrC particles as deformation nucleus and recrystallization nucleus enhances the nucleation rate of dynamic recrystallization of austenite and leads to grain refined with size of 34μm even when deformed at high temperature such as 1150 and 1050,further more that the ZrC particles as deformation nucleus increases concentrated degree of the located deformation in austenite makes deformation-induced ferrite transformation take place in advance at a higher temperature(950).Because a super-refined grain increases the critical cooling rate for obtaining martensite,the water-quenched microstructure deformed at the employed temperature developes from martensite to bainite and deformation-induced ferrite.Hardness analyses indicate that the hardening effect created by grain super-refining and strain is enough to offset the soft effect led by decrease in amount or even disappearance of martensite and bainite,also it can further increases the hardness of 20Mn2 steel to a higher value while the grain refining creates a bigger effect than the strain does.Analyses on the stress and strain in the deformation indicate that the austenite recrystallization causes a decrease in deformation resistance when deformed at 1150 and 1050,while deformation induced ferrite transformation plays the same role when deformed below 950.