Effect of Quenching Process on the Microstructure and Mechanical Property of 20mn2 Steel Containing ZrC Particles

刘志义,许晓嫦,邓小铁,李海

DOI: https://doi.org/10.3321/j.issn:1005-3093.2004.01.007

2004-01-01

Abstract:Effect of quenching process on the microstructure and mechanical property of 20Mn2 steel containing ZrC of 0.2% in volume fraction and 0.2-1.2μ m in diameter after rolling with large total reduction has been investigated. Experimental results show that when quenched in water, the mechanical property of 20Mn2 reaches σb=1854 MPa, σ0.2=1722 MPa, δ5=12.6%, after tempered at 200℃ for 200 min, σb=1685 MPa, σ0.2=1582 MPa, δ5=14.1%; while quenched in oil, σb=1073 MPa, σ0.2=839 MPa, δ5=19%, after tempered at 200℃ for 200min, σb=1039 MPa, σ0.2=810 MPa, δ5=21.1%. It is indicated that ZrC particle plays an obvious active role in grain super-refining of austenite by acting as a deformation nucleus and recrystallization nucleus, and obvious refined grain increases critical cooling rate for obtaining martensite that decreases the number, length and width of martensite in water-quenching state, and the number of pearlite in oil-quenching state, while the ferric carbide becomes shorter and thinner. Meanwhile, in subsequent cooling refined austenite grain transforms to a finer ferrite grain (1-2 μm), and keeps deformed microstructure in hot rolling, which leads to a double increase in the strength of 20Mn2 in water-quenching state without decrease in elongation, and a double increase in elongation of oil-quenching state with a concurrent great increase in the strength.