Abstract:The effect of rolling temperature on the incomplete recrystallization behavior and the relationship to mechanical properties in 0.06C–4Mn-1.2Cr (wt.%) steel was investigated. Three plates of experimental steel were produced by hot rolling at different temperatures and intercritical annealing processes in this study. The microstructure of experimental steels was examined by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscope (TEM). The mechanical properties of test steel were examined by impact test and tensile test. Austenite reversion and cementite precipitation-dissolution was numerically simulated under the assumption of local equilibrium. With the decrease of hot rolling temperature from 1000 °C to 800 °C, the uniform equiaxed prior austenite grains microstructures changed to heterogeneous microstructures of laminated and ultrafine prior austenite grains arranged alternatively. The tensile and impact tests revealed that the medium manganese steels rolling at 800 °C had an excellent combination of mechanical properties. Elongation had a great relationship with retained austenite fraction and stability. The fractography of impact specimens was examined to explore the toughening mechanism of the micro-laminated steels. The steel with uniform equiaxed grain structure exhibited a relatively low tensile strength of 750 MPa and low elongation of ∼20% and an extremely poor low-temperature toughness of ∼40 J at −40 °C. An enhanced low-temperature toughness (∼233 J at −40 °C), as well as an improved tensile strength (823 MPa) and higher elongation of ∼40%, was obtained in the steel with heterogeneous microstructures. The content of austenite in heterogeneous microstructure is twice that in uniform equiaxed grain structure. And cementite dissolved more thoroughly in the heterogeneous microstructure. The high austenite content of heterogeneous microstructures enabled the steel to be significantly stronger and ductile, which contributed to the high tensile strength and elongation to some extent. It is concluded that the effect of interface decohesion resulted in the occurrence of delamination. And the high austenite content and delamination greatly improved the low-temperature toughness of experimental steel.

The synergistic effect of grain refinement and precipitation strengthening on mechanical properties and dry sliding wear behavior of medium manganese steels

Precipitation Refinement via Aging Time Modification for Enhancing Wear Resistance in Ti–V–Nb Microalloyed High‐Manganese Steels

Effect of progressive solid-solution treatment on microstructures, mechanical properties and impact abrasive wear behavior of alloyed high manganese steel

Unraveling the significant role of retained austenite on the dry sliding wear behavior of medium manganese steel

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Effect of rolling temperature on microstructure and mechanical properties of medium manganese steel

Influence of Shot-peening Treatment on Wear Resistance of Medium Manganese Steel

Wear-Resistance Improvement of 65Mn Low-Alloy Steel through Adjusting Grain Refinement by Cyclic Heat Treatment

Wear properties of high-manganese steel strengthened with nano-sized V2C precipitates

Heterogeneous Multi-Phase Grains Improving the Strength-Ductility Balance in Warm-Rolled Fe-18Mn-3Ti Steel

Effect of Surface Impacting Parameters on Wear Resistance of High Manganese Steel

Effects of titanium addition on austenite grain size and mechanical properties of high manganese steel

Microstructure, Mechanical Properties and Wear Resistance of Low Alloy Abrasion Resistant Martensitic Steel Reinforced with TiC Particles

Microstructure evolution and mechanical properties of metastable austenitic medium Mn steel fabricated by warm caliber rolling

Effects of TiC and residual austenite synergistic strengthening mechanism on impact-abrasive wear behavior of bainite steel

Unusual grain-size effects on tensile deformation behavior of twinning-induced plasticity steel with low Mn content

Effect of Martensitic Reversal and Grain Size on the Corrosion and Wear Behaviour of Cr-Mn Steel

Yielding Behavior and Strengthening Mechanisms of a High Strength Ultrafine‐Grained Cr–Mn–Ni–N Stainless Steel

Importance of cold rolling and tempering on the microstructure evolution, precipitation behavior and mechanical responses of 9Cr3Co3W1Cu ferritic/martensitic steel

Microstructure, Precipitation and Mechanical Properties of a Titanium-Tungsten Alloyed Hot Rolled High Strength Steel

Effect of Heat Treatment Temperature on the Microstructure, Wear and Friction of Ni–Nb–V Alloyed Manganese Steel