Effect of Mo-coated MoS2 powder addition on the microstructure and properties of sintered Fe-15Cu-0.8C antifriction materials
Jiaxin Li,Kaichao Fu,Ruizhi Chen,Pengqi Chen,Jigui Cheng
DOI: https://doi.org/10.1007/s10853-023-09183-y
IF: 4.5
2023-12-13
Journal of Materials Science
Abstract:In this work, Mo-coated MoS 2 powders were prepared by a liquid phase coating-hydrogen reduction method with Mo improved the interfacial bonding between MoS 2 and ferrous materials. The sintered Fe-15Cu-0.8C antifriction materials containing Mo-coated MoS 2 powders, uncoated MoS 2 powders, and mechanically mixed Mo and MoS 2 powders were prepared. The influence of Mo-coated MoS 2 powder addition on microstructure and properties of the Fe-15Cu-0.8C antifriction materials were investigated. The results indicate that the microstructure of the sintered samples is mainly composed of ferrite, pearlite, copper, Fe 3 Mo 3 C, MoS 2 and pores. The hardness of the samples increases with increasing content of Mo and MoS 2 , due to the solid solution strengthening effect of Mo and the formation of the hard phase Fe 3 Mo 3 C. The MoS 2 particles wrapping with Mo decreases the reaction rate of MoS 2 with the matrix, resulting in improved bonding of the matrix. When the content of the Mo-coated MoS 2 powders is 3.75 wt.%, the hardness of the MoS 2 -reinforced Fe-15Cu-0.8C antifriction materials after Mo plating is optimized, which are 74.4 HRB. And the Fe-15Cu-0.8C materials containing 3.75 wt.% of Mo-coated MoS 2 revealed lower friction coefficient (0.065) at a sliding speed of 0.25 m/s and a load of 400 N. The present work has shown that the friction and wear propertied of the ferrous Fe-15Cu-0.8C materials can be effectively improved by the introducing of Mo-coated MoS 2 powders, while maintain relatively high mechanical properties, which shows potential uses in heavy load and high-speed applications.
materials science, multidisciplinary