Investigation on the Tribological Properties of FeS, Cu2S, MoS2, and WS2 Sulfide Films Under Water Lubrication
Jialin Wang,Bin Han,Zubin Chen,Chun Wang,Yongsheng Li,Anne Neville,Ardian Morina
DOI: https://doi.org/10.1080/10402004.2023.2201624
IF: 2.056
2023-04-29
Tribology Transactions
Abstract:FeS, MoS 2 , WS 2 , and Cu 2 S solid films were prepared on CoCrFeNiMo high entropy alloy (HEA), and their tribological performance was tested under water lubrication. The results show that the MoS 2 /CoCrFeNiMo and the Cu 2 S/CoCrFeNiMo composite coatings provided excellent tribological properties. The MoS 2 film of the MoS 2 /CoCrFeNiMo composite coating was not worn through at the load of 2 N, providing a reduction of 86% of friction coefficient ( μ = 0.03) and 69% of the wear rate (2.68 × 10 −9 cm 3 /Nm ), compared to CoCrFeNiMo coating. At a higher applied load, the anti-wear performance of MoS 2 film deteriorated because the MoS 2 reacted with oxygen and water to form α-MoO 3 . α-MoO3 hinders the sliding between layers of MoS 2 , increasing the third-body abrasive wear of the CoCrFeNiMo coating. Unlike the MoS 2 /CoCrFeNiMo composite coating, the Cu 2 S/CoCrFeNiMo composite coating exhibited an improved friction coefficient and wear rate at all loads. This performance is a result of Cu 2 S reacting with oxygen and water to form Cu and CuO, protecting the CoCrFeNiMo coating from severe wear.
engineering, mechanical