Abstract:This study investigated the effects of normalizing temperature, carburizing temperature, and time on the grain size and homogeneity of parent austenite grain (PAG) in 20CrMnTi gear steel. The grain coarsening mechanism was revealed to clarify the significance of normalizing temperature. The results manifested two different critical carburizing parameters that showed inverse grain evolutions at 940 and 800 °C normalizing temperatures, respectively. Compared to PAG without normalizing, the PAG size was smaller when the normalizing temperature was 940 °C for the carburizing temperature ≤ 970 °C and the holding time ≤ 4 h. Additionally, PAG with normalizing had a lower inhomogeneity factor than that without normalizing. When the carburizing process went beyond the critical carburizing parameters, grain coarsening and mixed grain appeared. Another critical carburizing parameter was transformed to a low temperature and a short time at 800 °C normalizing temperature. Additionally, under the same carburizing, the average grain size and mixed grain degree after normalizing at 940 °C were smaller than those at 800 °C. The redissolution and maturation of the (Nb, Ti, Mo)(C, N) particles during carburizing yielded grain coarsening and mixed grain phenomenon. The normalizing temperatures of 940 and 800 °C had little effect on the distribution of the (Nb, Ti, and Mo)(C, N) particles. However, the high-temperature normalizing at 940 °C generated fine and uniform austenite grains due to the microstructure heredity by reaustenitizing. Nevertheless, ferrite + austenite duple-phase microstructure was obtained at 800 °C, where the coarse ferrite grains increased the inhomogeneity of the austenite during carburizing.

Effect of carburizing process parameters on austenitic grain coarsening behavior of common carburizing steel

Effect of the Normalizing Temperature on the Size and Homogeneity of Austenite Grain in 20CrMnTi Carburized Gear Steel

Suppression of Austenite Grain Coarsening by Using Nb–Ti Microalloying in High Temperature Carburizing of a Gear Steel

Effect of Initial Microstructure on Austenite Transformation and Grain Growth Behavior of 20crmnti Steel During Pseudo-Carburizing Process

Effect of cyclic treatment after high temperature ion carburizing on austenite grain number and mechanical properties

On the grain coarsening behavior of 20CrMnTi gear steel during pseudo carburizing: A comparison of Nb-Ti-Mo versus Ti-Mo microalloyed steel

Microstructure Evolution and Mechanical Properties of High-Temperature Carburized 18Cr2Ni4WA Steel

Experimental Study on Vacuum Carburizing Process for Low-Carbon Alloy Steel

Effect of Cr and isothermal holding temperature on microstructure and properties of complex phase steel with high formability (CH steel)

Effect of Austenite Grain Coarsening on Rheological Behavior of Low-carbon High-strength Steel at High Temperature

Carburization-induced microstructure evolution and hardening mechanism of 18CrNiMo7-6 steel

Control of austenite grain size in a low carbon steel

Austenite grain growth behavior of medium carbon 34CrNiMo alloy steel during heating processes

Effect of Process Parameters on Microstructural Evolution and Grain Refinement in a Low Carbon High Strength Microalloyed Dual Phase Steel

Effect of microstructure on wear resistance during high temperature carburization heat treatment of heavy-duty gear steel

Suppress Austenite Grain Coarsening by Nb Alloying in High-Temperature-Pseudo-Carburized Bearing Steel

Effect of billet microstructure and deformation on austenite grain growth in forging heating of a medium-carbon microalloyed steel

Study on Decarburization Mechanism and Law of GCr15 Bearing Steel during Heat Treatment

Mechanical properties and cracking behavior of low-temperature gaseous carburized austenitic stainless steel

Carbonitride Dissolution And Austenite Grain Growth In A High Cr Ferritic Heat-Resistant Steel

Gradient microstructure evolution and hardening mechanism of carburized steel under novel heat treatment