Effect of billet microstructure and deformation on austenite grain growth in forging heating of a medium-carbon microalloyed steel

Fan Zhao,Hao Hu,Xinhua Liu,Zhihao Zhang,Jianxin Xie

DOI: https://doi.org/10.1016/j.jallcom.2021.159326

IF: 6.2

2021-07-01

Journal of Alloys and Compounds

Abstract:<p>We prepared samples with different ferrite-pearlite characteristics and deformation by heat treatment and Gleeble thermocompression respectively. Then, the different samples are rapidly heated to 1200 °C for 60 s to study the austenite grain growth. The study results show that the ferrite-pearlite characteristics has little effect on austenite grain growth. With the mean austenite grain size (MAGS) of billet microstructure increasing from 14 µm to 56 µm, the MAGS after heating only increases from 47 µm to 56 µm. With the cooling rate of billet samples increasing from 0.1 °C/s to 1.0 °C/s, the MAGS after heating has basically no change. However, the deformation of billet samples has significant effect on the austenite grain growth. With the deformation at 1150 °C increasing from 10% to 50%, the MAGS after heating decreases from 63 µm to 31 µm. In the meanwhile, the mean distance between element segregation bands decreases from 115 µm to 33 µm, and the mean width of element segregation bands decreases from 70 µm to 20 µm. Electron probe microanalysis shows that the segregation region has higher Si, Cr, Mn and V contents, which generate stronger solute drag effect on austenite grain boundaries. Deformation can crush the as-cast grains and make the segregation bands fine and dispersed, further refining the austenite grains after heating.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering