Effect of Deformation Degree on Microstructure and Properties of Ni-Based Alloy Forgings

Ruifeng Dong,Jian Li,Zishuai Chen,Wei Zhang,Xing Zhou
DOI: https://doi.org/10.3390/met14030340
IF: 2.695
2024-03-16
Metals
Abstract:The primary objective of this paper is to investigate the influence of deformation degree on the microstructure and properties of a Ni-based superalloy. An upsetting experiment was conducted using a free-forging hammer to achieve a deformation degree ranging from 60% to 80%. The impact of the forging deformation degree on the hardness and high-temperature erosion performance was evaluated using the Rockwell hardness tester (HRC) and high-temperature erosion tester, respectively. The experimental results indicate that as the deformation degree increased, the hardness of the forged material progressively increased while the rate of high-temperature erosion gradually decreased. In order to comprehensively study the mechanism behind the variations in forging performance, optical microscopy (OM), scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM) were employed. The findings reveal that as the deformation degree increased, the presence of small-angle grain boundaries and an increase in grain boundary area contributed to enhanced hardness in the alloy forgings. Furthermore, it was discovered that grain boundaries with twin orientation promoted dynamic recrystallization during deformation, specifically through a discontinuous dynamic recrystallization mechanism. Additionally, the precipitated γ′ phase in the alloy exhibited particle sizes ranging from 40 to 100 nm. This particle size range resulted in a higher critical shear stress value and a more pronounced strengthening effect on the alloy.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to study the influence of the degree of deformation on the microstructure and properties of nickel - based alloy forgings. Specifically, the paper mainly explores how the degree of deformation affects the hardness and high - temperature erosion properties of GH4738 nickel - based alloy. Through experiments, the author hopes to reveal the change mechanism of the alloy microstructure under different degrees of deformation and the specific influence of these changes on the alloy properties. ### Background of the paper - **Nickel - based alloys**: These alloys exhibit excellent resistance to deformation under high - temperature and high - stress conditions and are widely used in high - end equipment such as aero - engines. - **GH4738 alloy**: This is a precipitation - hardening deformed nickel - based alloy, which has excellent tensile strength and durability below 760 °C and excellent antioxidant properties below 870 °C. Due to its good crack - growth resistance and corrosion - resistance properties, the GH4738 alloy is widely used in turbine disk components of aero - engines. - **Challenge**: Since the GH4738 alloy contains a large number of strengthening phases (such as γ′ phase), it is very difficult to achieve a uniform distribution of the microstructure during the forging process. Therefore, optimizing the hot - deformation process parameters is crucial for controlling the grain size, γ′ - phase size and their distribution of the alloy. ### Experimental methods - **Material preparation**: The GH4738 alloy is prepared by vacuum consumable remelting (VAR) and vacuum induction melting (VIM). After blooming and homogenizing a 200 - mm billet, four small round bars with a diameter of 45 mm are extracted to ensure the consistency of the initial microstructure state. - **Hot - deformation experiment**: The small round bars are heated to 1140 °C, and then repeatedly upset using a 1 - ton free - forging hammer with deformation degrees of 60%, 68%, 72% and 80% respectively. The deformed disk - shaped forgings are cooled at the specified positions to ensure that their shapes are not deformed. - **Characterization methods**: - **Hardness test**: The hardness of the samples is tested using an HR - 150A Rockwell hardness tester. - **High - temperature erosion - wear test**: An ASTM G76 high - temperature erosion - wear testing machine is used, and the test conditions include an abrasive temperature of 750 °C, an abrasive speed of 88 m/s, an erosion angle of 90° and an erosion time of 20 seconds. - **Microstructure analysis**: The microstructure of the samples is analyzed in detail using an optical microscope (OM), a scanning electron microscope (SEM), electron back - scatter diffraction (EBSD) and a transmission electron microscope (TEM). ### Main findings - **Hardness change**: As the degree of deformation increases, the hardness of the alloy gradually increases. - **High - temperature erosion properties**: As the degree of deformation increases, the high - temperature erosion rate of the alloy gradually decreases. - **Microstructure changes**: - **Grain refinement**: An increase in the degree of deformation leads to a decrease in grain size, and no mixed - grain phenomenon occurs. - **Small - angle grain boundaries**: An increase in the degree of deformation leads to an increase in small - angle grain boundaries, which helps to increase the hardness of the alloy. - **Dynamic recrystallization**: The grain boundaries with twin orientations promote dynamic recrystallization, especially through the discontinuous dynamic recrystallization mechanism. - **γ′ - phase precipitation**: After deformation, the particle size of the γ′ - phase is between 40 and 100 nm, and this size range leads to a higher critical shear stress value, thereby enhancing the strengthening effect of the alloy. ### Conclusion This study reveals the microstructure evolution mechanism during the deformation process by systematically analyzing the influence of different degrees of deformation on the microstructure and properties of the GH4738 nickel - based alloy. These findings provide a theoretical basis for optimizing the hot - deformation process parameters, which helps to improve the comprehensive properties of the alloy and extend its service life.